Deposition of Thin Electroconductive Layers of Tin (II) Sulfide on the Copper Surface Using the Hydrometallurgical Method: Electrical and Optical Studies.

Thin films of tin (II) sulfide (SnS) were deposited onto a 500 µm thick copper substrate by a chemical bath method. The effect of sodium (Na) doping in these films was studied. The synthesis of the films was performed at temperatures of 60, 70, and 80 °C for 5 min.

Modulation of ODH Propane Selectivity by Zeolite Support Desilication: Vanadium Species Anchored to Al-Rich Shell as Crucial Active Sites.

The commercially available zeolite HY and its desilicated analogue were subjected to a classical wet impregnation procedure with NHVO to produce catalysts differentiated in acidic and redox properties. Various spectroscopic techniques (in situ probe molecules adsorption and time-resolved propane transformation FT-IR studies, XAS, V MAS NMR, and 2D COS UV-vis) were employed to study speciation, local coordination, and reducibility of the vanadium species introduced into the hierarchical faujasite zeolite. The acid-based redox properties of V centres were linked to catalytic activity in the oxidative dehydrogenation of propane.

The Properties of Cu Ions in Zeolites CuY Studied by IR Spectroscopy.

The properties of both Cu and Cu ions in zeolite CuY were followed with NO and CO as probe molecules. Cu was found to be located in S, S, and S sites, whereas Cu was found in S and S sites. The fine analysis of the spectra of Cu-NO and Cu-CO adducts suggests that both in S and in S sites two kinds of Cu cations exist.

Damage Development on the Surface of Nickel Coating in the Initial Period of Erosion.

The common occurrence of the phenomenon of cavitation in many industries and the multitude of factors affecting the resistance to cavitation erosion of used materials contribute to the search for methods and appropriate parameters of coating application that are able to minimize the effects of erosion. To determine the validity of the developed application parameters and the method used, cavitation studies and microscopic observations of the development of erosion during the cavitation test were carried out. There was a clear lack of incubation time and a linear increase in losses after 60 min of the test.

Polydispersity vs. Monodispersity. How the Properties of Ni-Ag Core-Shell Nanoparticles Affect the Conductivity of Ink Coatings.

The effect of polydispersity of nickel-silver core-shell nanoparticles (Ni-Ag NPs) on the conductivity of ink coatings was studied. Ni-Ag NPs of various average diameters (100, 220, and 420 nm) were synthesized and utilized for the preparation of conductive inks composed of monodisperse NPs and their polydisperse mixtures. The shell thickness of synthesized Ni-Ag NPs was found to be in the range of 10-20 nm and to provide stability of a core metal to oxidation for at least 6 months.

PDDA-Montmorillonite Composites Loaded with Ru Nanoparticles: Synthesis, Characterization, and Catalytic Properties in Hydrogenation of 2-Butanone.

The effect of synthesis parameters on the physicochemical properties of clay/ polydiallyldimethylammonium (PDDA)/Ru composites and their applicability in hydrogenation of 2-butanone under very mild conditions (room temperature, atmospheric pressure, and aqueous solution) was studied. Three synthetic procedures were employed, differing in the order of addition of components and the stage at which metallic Ru species were generated. The materials were characterized with XRD (X-ray diffraction), XRF (X-ray fluorescence), EDS (energy-dispersive spectroscopy), AFM (atomic force microscopy), TEM/HRTEM (transmission electron microscopy/high resolution transmission electron microscopy), and TG/DSC (thermal gravimetry/differential scanning microscopy techniques.

Simultaneous removal of dyes and metal cations using an acid, acid-base and base modified vermiculite as a sustainable and recyclable adsorbent.

The aim of this work was the modification of vermiculite in order to produce a low cost, efficient and sustainable adsorbent for dyes and metals. Three activation methods consisting of acid, base and combined acid/base treatment were applied to improve the of vermiculite's adsorption properties. Adsorbents were tested in single, bi- and tricomponent solutions containing cationic dyes and Cu cations.