Nanoparticle loading level and properties of experimental hybrid resin luting agents.

Purpose: This study investigated the influence of nanoparticle loading level on properties of experimental hybrid resin luting agents.

Materials And Methods: Silanated 2-μm barium borosilicate glass microparticles and 7-nm silica nanoparticles were used. Five materials were obtained by loading a photocurable Bis-GMA/TEGDMA co-monomer with a total mass fraction of 60% inorganic fillers.

The effect of repeated firings on the color of feldspathic ceramics.

The aim of this study was to determine the extent to which repeated firings would change the color of feldspathic ceramics. Specimens were fabricated from five commercially available feldspathic ceramics using a circular stainless steel matrix 11 mm in diameter and 1.0 mm thick (n = 10, shade = A3).

Resin-dentin bond strength of 10 contemporary etch-and-rinse adhesive systems after one year of water storage.

To compare the resin-dentin bond degradation of 10 contemporary etch-and-rinse adhesive systems after one year of water storage, 100 bovine incisors were randomly separated into 10 groups and their superficial coronal dentin was exposed. According to manufacturers' instructions, dentin surfaces were bonded with one of seven two-step etch-and-rinse adhesives or one of three three-step etch-and-rinse adhesives. Composite buildups were constructed incrementally.

Fracture resistance of premolars restored with inlay and onlay ceramic restorations and luted with two different agents.

Purpose: The purpose of this study was to evaluate the fracture resistance of human maxillary premolars restored with 2 ceramic systems (Vitadur Alpha and In Ceram) comparing 3 preparation designs and 2 luting agents.

Methods: Seventy sound teeth were prepared to receive ceramic restorations (Vitadur Alpha; n=14) as follows: (1) control, sound premolars, with no preparation, (2) inlays, (3) partial onlays (palatal cuspid coverage), (4) total onlays (both cuspids coverage), and (5) total onlays with an In Ceram core. The ceramic restorations were cemented using Enforce or RelyX ARC (half restorations with each cement), placed into the cavity and held under pressure, except for the control group.