Adhesive Bioactive Coatings Inspired by Sea Life.

Inspired by nature, in particular by the marine mussels adhesive proteins (MAPs) and by the tough brick-and-mortar nacre-like structure, novel multilayered films are prepared in the present work. Organic-inorganic multilayered films, with an architecture similar to nacre based on bioactive glass nanoparticles (BG), chitosan, and hyaluronic acid modified with catechol groups, which are the main components responsible for the outstanding adhesion in MAPs, are developed for the first time. The biomimetic conjugate is prepared by carbodiimide chemistry and analyzed by ultraviolet-visible spectrophotometry.

Nanostructured polymeric coatings based on chitosan and dopamine-modified hyaluronic acid for biomedical applications.

In a marine environment, specific proteins are secreted by mussels and used as a bioglue to stick to a surface. These mussel proteins present an unusual amino acid 3,4-dihydroxyphenylalanine (known as DOPA). The outstanding adhesive properties of these materials in the sea harsh conditions have been attributed to the presence of the catechol groups present in DOPA.

A nanotectonics approach to produce hierarchically organized bioactive glass nanoparticles-based macrospheres.

Bioactive particles have been widely used in a series of biomedical applications due to their ability to promote bone-bonding and elicit favorable biological responses in therapies associated with the replacement and regeneration of mineralized tissues. In this work hierarchical architectures are prepared by an innovative methodology using SiO(2)-CaO sol-gel based nanoparticles. Inspired by colloidal crystals, spherical aggregates were formed on biomimetic superhydrophobic surfaces using bioactive glass nanoparticles (BG-NPs) able to promote bone regeneration.

Chitosan/bioactive glass nanoparticles composites for biomedical applications.

Nanocomposite films based on a chitosan blend with bioactive glass nanoparticles (BG-NPs) with different formulations, namely SiO(2):CaO:P(2)O(5)(mol.%) = 55:40:5 and SiO(2):CaO:P(2)O(5):MgO(mol.%) = 64:26:5:5 were produced in order to develop systems with applicability in guided tissue regeneration.

Chitosan/bioactive glass nanoparticle composite membranes for periodontal regeneration.

Barrier membranes are used in periodontal applications with the aim of supporting periodontal regeneration by physically blocking migration of epithelial cells. The present work proposes a combination of chitosan (CHT) with bioactive glass nanoparticles (BG-NPs) in order to produce a novel guided tissue and bone regeneration membrane, fabricated by solvent casting. The CHT/BG-NP nanocomposite membranes are characterized in terms of water uptake, in mechanical tests, under simulated physiological conditions and in in vitro bioactivity tests.

Micropatterning of bioactive glass nanoparticles on chitosan membranes for spatial controlled biomineralization.

Bioactive glass nanoparticles (BG-NPs) capable of inducing apatite precipitation upon immersion in simulated body fluid (SBF) were patterned on free-standing chitosan membranes by microcontact printing using a poly(dimethylsiloxane) (PDMS) stamp inked in a BG-NPs pad. Formation of the patterns was characterized by scanning electron microscopy (SEM). Mineralization of the bioactive glass patterns was induced in vitro by soaking the samples in SBF over different time points up to 7 days.

Preparation and characterization of bioactive glass nanoparticles prepared by sol-gel for biomedical applications.

Bioactive glass nanoparticles (BG-NPs), based on both ternary (SiO(2)-CaO-P(2)O(5)) and binary (SiO(2)-CaO) systems, were prepared via an optimized sol-gel method. The pH of preparation and the effect of heat treatment temperature were evaluated, as well as the effect of suppressing P in the bioactivity ability of the materials. The morphology and composition of the BG-NPs were studied using FTIR, XRD and SEM.

Mono-dispersed bioactive glass nanospheres: preparation and effects on biomechanics of mammalian cells.

Mono-dispersed SiO(2)-CaO bioactive glass nanospheres (BGNS) were prepared by a two step sol-gel method in the absence of surfactant. The size of BGNS ranged from 200 to 350 nm in diameter and exhibited a rough surface texture. In vitro biomineralization tests showed that BGNS could rapidly induce the deposition of an apatite layer in simulated body fluid (SBF).

Biomimetic design of materials and biomaterials inspired by the structure of nacre.

The micro-architecture of nacre (mother of pearl) has been classically illustrated as a 'brick-and-mortar' arrangement. It is clear now that hierarchical organization and other structural features play an important role in the amazing mechanical properties of this natural nanocomposite. The more important structural characteristics and mechanical properties of nacre are exposed as a base that has inspired scientists and engineers to develop biomimetic strategies that could be useful in areas such as materials science, biomaterials development and nanotechnology.