Directed Self-Assembly of Lamellar Copolymers: Effects of Interfacial Interactions on Domain Shape.

The depth-dependent structure of a poly(styrene--methylmethacrylate) (PS-PMMA) line grating (46 nm pitch) was calculated from quantitative analysis of small-angle X-ray scattering profiles. These data demonstrate that domain shapes are significantly deformed near the substrate interface, where the local PS domain shape resembles an hourglass. The bulk equilibrium dimension is recovered near the center of a 64 nm thick film.

Impact of film thickness on the morphology of mesoporous carbon films using organic-organic self-assembly.

Mesoporous polymer and carbon thin films are prepared by the organic-organic self-assembly of an oligomeric phenolic resin with an amphiphilic triblock copolymer template, Pluronic F127. The ratio of resin to template is selected such that a body-centered cubic (Im3m) mesostructure is formed in the bulk. However, well-ordered mesoporous films are not always obtained for thin films (<100 nm), and this behavior is found to be directly correlated with the initial phenolic resin to template ratio.