Influence of Cr Content on the High-Temperature Oxidation Behavior and Mechanism of Low-Alloy Steels.

The high-temperature oxidation behavior of low-carbon steel (AISI 1015, AISI 8617, AISI 4115) was investigated over the temperature range from 600 to 1000 °C in humid air containing 25% water vapor. Mass gain of oxidation measurement was performed to study the oxidation kinetics. The microstructure, thickness, and composition of the oxide scale formed were investigated via optical microscope (OM), scanning electron microscope (SEM) equipped with an energy dispersive spectrometer (EDS), X-ray diffraction (XRD), and electron probe microanalyzer (EPMA).