Role of the entangled amorphous network in tensile deformation of semicrystalline polymers.

Being composed of crystalline lamellae and entangled amorphous polymeric chains in between, semicrystalline polymers always show a complicated deformation behavior under tensile deformation. In recent years, the process of tensile deformation was found to exhibit several regimes: intralamellar slipping of crystalline blocks occurs at small deformation whereas a stress-induced crystalline block disaggregation-recrystallization process occurs at a strain larger than the yield strain. The strain at this transition point is related to the interplay between the amorphous entanglement density and the stability of crystal blocks.