In situ measurement of damage evolution in shocked magnesium as a function of microstructure.

Accurate modeling and prediction of damage induced by dynamic loading in materials have long proved to be a difficult task. Examination of postmortem recovered samples cannot capture the time-dependent evolution of void nucleation and growth, and attempts at analytical models are hindered by the necessity to make simplifying assumptions, because of the lack of high-resolution, in situ, time-resolved experimental data. We use absorption contrast imaging to directly image the time evolution of spall damage in metals at ∼1.

Thermomechanics of nanocrystalline nickel under high pressure-temperature conditions.

We present a comparative study of thermomechanical properties of nano-polycrystalline nickel (nano-Ni) and micrometer-polycrystalline nickel (micron-Ni) by in situ high pressure-temperature (P-T) diffraction experiments. The yield strength of 2.35 GPa for the nano-Ni measured under high-pressure triaxial compression is more than three times that of the micron-Ni value.