Novel Efficient Reduction Route for Magnesium Production Using Silicothermic Process.

A novel efficient reduction route was developed for preparing porous pellets to enhance mass transfer during magnesium production, which can improve the reactivity of pellet reaction to improve the reduction efficiency. A porous pellet precursor was prepared at 150 MPa using NHHCO as a pore-forming agent, and the reaction characteristics of the pellets with 0, 5%, 10%, 20%, and 30% pore-forming agents were measured under a high vacuum of approximately 10 Pa heat-treated from 100 °C to 1400 °C. The results showed that the instantaneous maximum reduction rate first increased and then decreased with the increase in pore-forming agents.