Comparative study of iodine-doped and undoped pyrrole grafting with plasma on poly (glycerol sebacate) scaffolds and its human dental pulp stem cells compatibility.

This study addresses the morphological and chemical characterization of PGS scaffolds after (6, 12, 18, 24, and 30 min) residence in undoped pyrrole plasma (PGS-PPy) and the evaluation of cell viability with human dental pulp stem cells (hDPSCs). The results were compared with a previous study that used iodine-doped pyrrole (PGS-PPy/I). Analyses through SEM and AFM revealed alterations in the topography and quantity of deposited PPy particles.

Effect of different exposure times on physicochemical, mechanical and biological properties of PGS scaffolds treated with plasma of iodine-doped polypyrrole.

Polyglycerol sebacate (PGS) scaffolds obtained using a leaching technique were modified with iodine-doped polypyrrole (PPy-I) in a plasma reactor in order to study the effect of exposure time on the cell viability of hDPSCs. SEM analysis showed the formation and growth of PPy-I particles as the exposure time was increased, while FTIR and XPS analysis revealed the presence of -NH- and N+ groups in the chemical composition of the surfaces, relating to the increase in the amount of PPY-I particles. The water contact angle measurements showed an increase in the scaffold's hydrophilicity with greater exposure times which was also attributed to the rising of PPy-I particles.