Dynamics of the Interaction Between Ceria and Platinum During Redox Processes.

The work is focused on understanding the dynamics of the processes which occur at the interface between ceria and platinum during redox processes, by investigating an inverse catalytic model system made of ceria epitaxial islands and ultrathin films supported on Pt(111). The evolution of the morphology, structure and electronic properties is analyzed in real-time during reduction and oxidation, using low-energy electron microscopy and spatially resolved low-energy electron diffraction. The reduction is induced using different methods, namely thermal treatments in ultra-high vacuum and in H as well as deposition of Ce on the oxide surface, while re-oxidation is obtained by exposure to oxygen at elevated temperature.

Electronic properties of epitaxial cerium oxide films during controlled reduction and oxidation studied by resonant inelastic X-ray scattering.

We investigated the evolution of the electronic structure of cerium oxide ultrathin epitaxial films during reduction and oxidation processes using resonant inelastic X-ray scattering at the Ce L3 absorption edge, a technique sensitive to the electronic configurations at the 4f levels and in the 5d band thanks to its high energy resolution. We used thermal treatments in high vacuum and in oxygen partial pressure to induce a controlled and reversible degree of reduction in cerium oxide ultrathin epitaxial films of different thicknesses. Two dominant spectral components contribute to the measured spectra at the different degrees of oxidation/reduction.

Morphology, structural properties and reducibility of size-selected CeO2- x nanoparticle films.

Non-stoichiometric ceria nanoparticles (NPs) were obtained by a gas aggregation source with a magnetron and were mass-selected with a quadrupole mass filter. By varying magnetron power, Ar gas flow, and the length of the aggregation tube, NPs with an average diameter of 6, 9, and 14 nm were synthesized and deposited onto a substrate, thus obtaining NP films. The morphology of the films was studied with scanning electron microscopy, while high resolution transmission electron microscopy was used to gain a deeper insight into the atomic structure of individual NPs.