Thermal, magnetic and electronic properties of non-centrosymmetric YbPt₂B.

Ternary YbPt2B crystallizes in the non-centrosymmetric hexagonal CePt2B-type structure (space group P6(2)22). Electrical resistivity, specific heat and magnetic measurements reveal a magnetic instability at 5.6 K.

Structural and physical properties diversity of new CaCu5-type related europium platinum borides.

Three novel europium platinum borides have been synthesized by arc melting of constituent elements and subsequent annealing. They were characterized by X-ray powder and single-crystal diffraction: EuPt4B, CeCo4B type, P6/mmm, a = 0.56167(2) nm, c = 0.

Magnetically interacting low dimensional Ni-nanostructures within porous silicon.

Electrodeposition of ferromagnetic metals, a common method to fabricate magnetic nanostructures, is used for the incorporation of Ni structures into the pores of porous silicon templates. The porous silicon is fabricated in various morphologies with average pore-diameters between 40 and 95 nm and concomitant pore-distances between 60 and 40 nm. The metal nanostructures are deposited with different geometries as spheres, ellipsoids or wires influenced by the deposition process parameters.

On the physical properties of RPd(8)B(2-x) and R(3)Pd(25-x)B(8-y) (R = La, Ce).

Physical properties (magnetization, electrical resistivity and specific heat in the temperature range from 2 to 270 K (0.3-270 K for the resistivity)) have been determined for polycrystalline samples of the ternary compounds RPd(8)B(2 - x) (CePd(8)B(2 - x) type; space group C 2/c) and R(3)Pd(25 - x)B(8 - y) (La(3)Pd(25 - x)B(8 - y) type; space group P 2(1)/c) with R = La, Ce. Rietveld refinement of x-ray powder intensity data confirmed the crystal structure and single-phase condition.

Phase formation and ground state properties of CeCo₉Si₄.

The phase relations of the CeCo(9 + δ)Si(4 - δ) system have been studied by means of scanning electron microscopy, electron microprobe analysis and x-ray diffraction. Essentially single phase samples CeCo(9 + δ)Si(4 - δ) (structure-type LaFe(9)Si(4) with space group I4/mcm) are formed in a narrow composition range - 0.3 ≤ δ < 0.