Effect of epigallocatechin-3-gallate and thermal cycling on the bond strength of resin cements to the root dentin.

This study evaluated the effect of epigallocatechin-3-gallate (EGCG) solution and thermal cycling on the bond strength (BS) of fiber posts to the root dentin using two different resin cements (conventional or self-adhesive). One hundred and forty-four bovine roots were endodontically treated. After post space preparation, specimens were randomly divided into six groups (n = 24) according to dentin pretreatment [distilled water, 0.

Influence of Sealer and Light-Curing Units on Push-Out Bond Strength Of Composite Resin to Weakened Roots.

The aim of this study was to assess the influence of sealer and light-curing unit on regional bond strength of resin composite to the weakened roots. Ninety roots of incisors were experimentally weakened, subjected to biomechanical preparation and filled with either Endofill, AH Plus or MTA Fillapex The roots were desobturated e reinforced with resin composite and fiber post light-activated with one of the light sources: halogen at 600 mW/ cm2 (QTH-600), LED at 800 mW/ cm2 (LED-800) and LED at 1500 mW/ cm2 (LED-1500). The roots were sectioned in slices from cervical, middle and apical root-reinforcement regions and analyzed by push out test, scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM).

1064-nm Nd:YAG and 980-nm Diode Laser EDTA Agitation on the Retention of an Epoxy-Based Sealer to Root Dentin.

Root canal irrigants are used to minimize the negative effects of smear layer on endodontic sealer retention. The aim of this study was to evaluate the efficacy of agitation of 17% ethylenediaminetetraacetic acid (EDTA) with ultrasonic, 1064-nm Nd:YAG and 980-nm diode laser on the retention of an epoxy-based sealer to the root canal walls. Forty single-rooted bovine teeth were instrumented with ProTaper rotary system and divided into four groups according to the final irrigation protocol (n = 10): (1) 17% EDTA (control); (2) 17% EDTA with 50-s ultrasonic agitation; (3) 17% EDTA with 50-s diode laser (2-W) agitation; and (4) 17% EDTA with 50-s Nd:YAG (1.