[Synthesis and luminescence properties of Mg2Y8Si6O26 : Ce3+, Mn2+ phosphor].

Mg2Y8Si6O26 : Ce3+, Mn2+ phosphor was synthesized by the high temperature solid-state reaction, and the structure and luminescence properties were characterized by X-ray diffraction (XRD) and fluorescence spectrophotometer. The XRD pattern demonstrated that the synthetic material belongs to the hexagonal phase of Mg2Y8Si6O26 crystal without detectable impurity and space group P6(3)/m. The excitation and emission spectrum showed that there exist two lattice positions for Ce3+ in Mg2Y8Si6O26 crystal and their luminescence properties were compared.

[Synthesis and upconversion luminescence properties of BaIn6 Y2O13 : Yb3+, Er3+].

BaIn6 Y2O13 phosphors with different doping concentrations of Yb3+ and Er3+ were prepared via the high temperature solid-state reaction method. XRD data showed that BaIn6 Y2O13 phosphors belong to hexagonal system and the introduction of doping agent Yb3+ and Er3+ did not change the lattice structure of the host. The upconversion emission spectrum and power were measured by 971 nm LD laser with different excitation powers and the energy efficiencies of the samples were calculated.

[Preparation and up-conversion luminescence dynamic process of Yb3+/ Er3+ co-doped BaGd2ZnO5].

Yb3+/Er3+ co-doped BaGd2 ZnO5 phosphors were prepared by using the sol-gel method. The up-conversion luminescence powers and efficiencies were measured under different excitation densities. The obtained data showed that the green luminescence power was proportional to the second-order of that of the excitation power under the lower excitation density and linearly in the higher one.