On the morphology and stability of Au nanoparticles on TiO2(110) prepared from micelle-stabilized precursors.

The morphology and stability of well-ordered, nanostructured Au/TiO2(110) surfaces, prepared by deposition of Au loaded micelles on TiO2(110) substrates and subsequent oxidative removal of the polymer shell in an oxygen plasma, was investigated by noncontact AFM, SEM and XPS. The resulting arrays of Au nanoparticles (particle sizes 1-5 nm) form a nearly hexagonal pattern with well-defined interparticle distances and a narrow particle size distribution. Particle size and particle separation can be controlled independently by varying the Au loading and the block-copolymers in the micelle shell.

From colloidal Co/CoO core/shell nanoparticles to arrays of metallic nanomagnets: surface modification and magnetic properties.

The magnetic properties of nanoparticles can be subject to strong variations as the chemical composition of the particle surface is modified. To study this interrelation of surface chemistry and magnetism, self-assembled layers of colloidal 9.5 nm Co/CoO core/shell nanoparticles were exposed to mild reactive hydrogen and oxygen plasmas.