Smart membranes by electron beam cross-linking of copolymer microgels.

Poly(N-isopropylacrylamide) (pNIPAM) based copolymer microgels were used to create free-standing, transferable, thermoresponsive membranes. The microgels were synthesized by copolymerization of NIPAM with N-benzylhydrylacrylamide (NBHAM). Monolayers of these colloidal gels were subsequently cross-linked using an electron gun leading to the formation of a connected monolayer.

Surface-Enhanced Raman Spectroscopy of Carbon Nanomembranes from Aromatic Self-Assembled Monolayers.

Surface-enhanced Raman scattering spectroscopy (SERS) was employed to investigate the formation of self-assembled monolayers (SAMs) of biphenylthiol, 4'-nitro-1,1'-biphenyl-4-thiol, and p-terphenylthiol on Au surfaces and their structural transformations into carbon nanomembranes (CNMs) induced by electron irradiation. The high sensitivity of SERS allows us to identify two types of Raman scattering in electron-irradiated SAMs: (1) Raman-active sites exhibit similar bands as those of pristine SAMs in the fingerprint spectral region, but with indications of an amorphization process and (2) Raman-inactive sites show almost no Raman-scattering signals, except a very weak and broad D band, indicating a lack of structural order but for the presence of graphitic domains. Statistical analysis showed that the ratio of the number of Raman-active sites to the total number of measurement sites decreases exponentially with increasing the electron irradiation dose.