Effects of cigarette smoke on color, roughness and gloss of high-viscosity bulk-fill resin composites.

Purpose: To evaluate the effect of cigarette smoke (CS) on color, roughness and gloss of bulk-fill resin composites.

Methods: Resin discs (10 x 2 mm) were made for resin composites (n= 10) : Filtek Z250XT (control), Filtek One Bulk Fill (FOBF), Tetric N-Ceram Bulk-Fill (TBF) and Aura Bulk-Fill (ABF). The color ( ΔL*, Δa*, Δb*, ΔE and ΔE00), roughness (Ra) and gloss analyses were performed at the baseline and after CS exposure (10 packs of cigarettes - Marlboro Red).

Influence of pre-heating and ceramic thickness on physical properties of luting agents.

Purpose: The objective of this in vitro study was to evaluate the influence of ceramic thickness and pre-heating of luting agents on their physical properties.

Materials And Methods: The materials RelyX Arc, RelyX Ultimate, RelyX Veneer, and Filtek Z350 Flow were handled at different temperatures (23°C or 54°C), inserted into matrix, and photoactivated through ceramic disks (0.75 mm or 1.

Influence of surface treatments on enamel susceptibility to staining by cigarette smoke.

Objectives: The purpose of this study was to evaluate the influence of remineralizing agents, including artificial saliva, neutral fluoride, and casein phosphopeptide-amorphous calcium phosphate (CPP-ACP), on the susceptibility of bleached enamel to staining by cigarette smoke.

Study Design: Fifty bovine enamel blocks were randomly divided into five groups (n = 10): G1- bleaching; G2- bleaching and immersion in artificial saliva; G3- bleaching and application of CPP-ACP; G4- bleaching and application of neutral fluoride; and G5- untreated (Control). Teeth were bleached with 35% hydrogen peroxide and treated with the appropriate remineralizing agent.

Influence of light curing and sample thickness on microhardness of a composite resin.

The aim of this in vitro study was to evaluate the influence of light-curing units and different sample thicknesses on the microhardness of a composite resin. Composite resin specimens were randomly prepared and assigned to nine experimental groups (n = 5): considering three light-curing units (conventional quartz tungsten halogen [QTH]: 550 mW/cm(2) - 20 s; high irradiance QTH: 1160 mW/cm(2) - 10 s; and light-emitting diode [LED]: 360 mW/cm(2) - 40 s) and three sample thicknesses (0.5 mm, 1 mm, and 2 mm).