Microstructure and physical properties of black-aluminum antireflective films.

The microstructure and physical properties of reflective and black aluminum were compared for layers of different thicknesses deposited by magnetron sputtering on fused silica substrates. Reflective Al layers followed the Volmer-Weber growth mechanism classically observed for polycrystalline metal films. On the contrary, the extra nitrogen gas used to deposit the black aluminum layers modified the growth mechanism and changed the film morphologies.

Preparation and Characteristics of High-Performance, Low-Density Metallo-Ceramics Composite.

By applying the physical vapour deposition method, hollow ceramic microspheres were coated with titanium, and subsequently, they were sintered using the spark plasma sintering technique to create a porous ceramic material that is lightweight and devoid of a matrix. The sintering process was carried out at temperatures ranging from 1050 to 1200 °C, with a holding time of 2 min. The samples were subjected to conventional thermal analyses (differential scanning calorimetry, thermogravimetry, dilatometry), oxidation resistance tests, and thermal diffusivity measurements.

High-Temperature Corrosion Behavior of Selected HVOF-Sprayed Super-Alloy Based Coatings in Aggressive Environment at 800 °C.

This study is focused on the high-temperature corrosion evaluation of selected thermally sprayed coatings. NiCoCrAlYHfSi, NiCoCrAlY, NiCoCrAlTaReY, and CoCrAlYTaCSi coatings were sprayed on the base material 1.4923.

Hot Corrosion Behavior of TWAS and HVOF NiCr-Based Coatings in Molten Salt.

In order to extend the life of boilers by applying an anti-corrosion coating without the need to dismantle them, it is advisable to find coatings that can be applied using cheaper and portable techniques, such as Twin Wire Arc Spray technology (TWAS). In this study, we compare selected NiCr-based coatings and two uncoated steel substrates (steel 1.7715 and 1.

Dielectric Spectroscopy of Calcium Titanate Processed by Spark Plasma Sintering.

Calcium titanate (CaTiO) powder was compacted by spark plasma sintering (SPS). The resulting products were subjected to the phase stability study and dielectric characterization. The change in temperature of SPS between 1100 °C and 1250 °C had a clear and straightforward effect on density, porosity, relative permittivity, loss tangent, and DC resistivity.