γ-Ray-Induced Degradation in the Triple-Cation Perovskite Solar Cells.

We report on the impact of γ radiation (0-500 Gy) on triple-cation CsMAFAPb(BrI) perovskite solar cells. A set of experiments was designed to reveal the individual contributions of the hole-collecting bottom electrode, perovskite absorber, and electron transport layer (ETL) to the overall solar cell degradation under radiation exposure. We show that the glass/ITO/PEDOT:PSS hole-collecting electrode withstands a 500 Gy dose without any losses in the solar cell performance.