In situ ultrasonic diagnostic of zeolite X crystallization with novel (hierarchical) morphology from coal fly ash.

In this paper the applicability of an in situ ultrasonic diagnostic technique in understanding the formation process of zeolite X with a novel morphology was demonstrated. The complexity of the starting fly ash feedstock demands independent studies of the formation process for each type of zeolite since it is not known whether the crystallization mechanism will always follow the expected reaction pathway. The hierarchical zeolite X was noted to follow a solution phase-mediated crystallization mechanism which differs from earlier studies of the zeolite A formation process from unaged, clear solution extracted from fused fly ash.

Optimization of hydrothermal synthesis of pure phase zeolite Na-P1 from South African coal fly ashes.

This study was aimed at optimizing the synthesis conditions for pure phase zeolite Na-P1 from three coal fly ashes obtained from power stations in the Mpumalanga province of South Africa. Synthesis variables evaluated were: hydrothermal treatment time (12-48 hours), temperature (100-160°C) and varying molar quantities of water during the hydrothermal treatment step (H(2)O:SiO(2) molar ratio ranged between 0-0.49).

Synthesis of hydroxy sodalite from coal fly ash using waste industrial brine solution.

The effect of using industrial waste brine solution instead of ultra pure water was investigated during the synthesis of zeolites using three South African coal fly ashes as Si feedstock. The high halide brine was obtained from the retentate effluent of a reverse osmosis mine water treatment plant. Synthesis conditions applied were; ageing of fly ash was at 47 ° C for 48 hours, and while the hydrothermal treatment temperature was set at 140 ° C for 48 hours.