Local Degradation Mechanisms by Tarnishing of Protected Silver Mirror Layers Studied by Combined Surface Analysis.

In this work, we addressed the local degradation mechanisms limiting the prelaunch environmental durability of thin-layered silver stacks for demanding space mirror applications. Local initiation and propagation of tarnishing were studied by combined surface and interface analysis on model stack samples consisting of thin silver layers supported on lightweight SiC substrates and protected by thin SiO overcoats, deposited by cathodic magnetron sputtering and submitted to accelerated aging in gaseous HS. The results show that tarnishing is locally initiated by the formation of AgS columns erupting above the stack surface.