Formation of Grown-In Nitrogen Vacancies and Interstitials in Highly Mg-Doped Ammonothermal GaN.

The formation of intrinsic point defects in the N-sublattice of semi-insulating Mg-doped GaN crystals grown by the ammonothermal method (SI AT GaN:Mg) was investigated for the first time. The grown-in defects produced by the displacement of nitrogen atoms were experimentally observed as deep traps revealed by the Laplace transform photoinduced transient spectroscopy in the compensated -type crystals with the Mg concentrations of 6 × 10 and 2 × 10 cm and resistivities of ~10 Ωcm and ~10 Ωcm, respectively. In both kinds of materials, three closely located traps with activation energies of 430, 450, and 460 meV were revealed.

Negative Magnetoresistivity in Highly Doped n-Type GaN.

This paper presents low-temperature measurements of magnetoresistivity in heavily doped n-type GaN grown by basic GaN growth technologies: molecular beam epitaxy, metal-organic vapor phase epitaxy, halide vapor phase epitaxy and ammonothermal. Additionally, GaN crystallized by High Nitrogen Pressure Solution method was also examined. It was found that all the samples under study exhibited negative magnetoresistivity at a low temperature (10 K < T < 50 K) and for some samples this effect was observed up to 100 K.

Effects of MOVPE Growth Conditions on GaN Layers Doped with Germanium.

The effect of growth temperature and precursor flow on the doping level and surface morphology of Ge-doped GaN layers was researched. The results show that germanium is more readily incorporated at low temperature, high growth rate and high V/III ratio, thus revealing a similar behavior to what was previously observed for indium. V-pit formation can be blocked at high temperature but also at low V/III ratio, the latter of which however causing step bunching.