Mechanical and Thermal Properties of Polylactide (PLA) Composites Modified with Mg, Fe, and Polyethylene (PE) Additives.

In this article, polylactic acid-based composites reinforced with 5% of polyethylene, iron, and magnesium powders were prepared by extrusion and compressed under the pressure of about 10 MPa and characterized. These composites were mechanically, thermally, and morphologically evaluated. It was found, compared to the pure polylactic acid (PLA), an improvement in tensile strength (both σ and YS) was obtained for the composite with the iron powder addition, while the magnesium powder slightly improved the ductility of the composite material (from 2.

Microstructure, Mechanical, and Corrosion Properties of Ni-Free Austenitic Stainless Steel Prepared by Mechanical Alloying and HIPping.

An influence of the powder metallurgy route on the phase structure, mechanical properties, and corrosion resistance of Fe-18%Cr-12%Mn-N nickel-free austenitic stainless steel as a potential material for medical applications were studied. The powder was mechanically alloyed in a high purity nitrogen atmosphere for 90 h followed by Hot Isostatic Pressing at 1150 °C (1423 K) and heat treatment at 1175 °C (1423 K) for 1 h in a vacuum with furnace cooling and water quenching. More than 96% of theoretical density was obtained for the samples after Hot Isostatic Pressing that had a direct influence on the tensile strength of the tested samples (Ultimate Tensile Strength is 935 MPa) with the total elongation of 0.