Knoop hardness and effectiveness of dual-cured luting systems and flowable resin to bond leucite-reinforced ceramic to enamel.

Purpose: The aim of this study was to evaluate the Knoop microhardness and microshear bond strength (MSBS) of dual-cured luting systems and flowable resin bonded to leucite-reinforced ceramics and enamel.

Materials And Methods: Eighty bovine incisors were randomly divided into four groups per test (microhardness and microshear; n = 10) according to the bonding procedure: Excite DSC/Variolink, Clearfil SE Bond/Panavia F, Adper Scotchbond Multi-Purpose Plus/RelyX ARC, and Adper Single Bond 2/Filtek Z350 Flow. For the KHN measurement, the cement was applied on the enamel surface and light-cured through a ceramic disk (5 mm diameter × 1.

Influence of the curing mode on the degree of conversion of a dual-cured self-adhesive resin luting cement beneath ceramic.

Objective: To evaluate the effect of the delayed photoactivation and ceramic barrier on the degree of conversion (DC) of self-adhesive resin cement.

Materials And Methods: Circular specimens (5 mm in diameter × 1 mm in thickness) of the RelyX U-100 resin cement were made using the following curing protocols (n = 10): (G1) 40 s beneath a IPS Empress II ceramic; (G2) 40 s of direct photocuring; (G3) 80 s beneath the ceramic; (G4) 80 s of direct photocuring; (G5) self-curing; (G6) 5 min in the absence of light (self-curing) followed by transceramic photocuring for 40 s; (G7) 5 min in the absence of light (self-curing) followed by transceramic photocuring for 80 s. All the specimens were photoactivated by LED (800 mW/cm(2)).