Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic.

Introduction: Based on the importance of the integrity of the metal/ceramic interface, the purpose of this work was to evaluate the shear bond strength of the metal-ceramic union of two Co-Cr alloys (Wirobond C, Bego; Remanium 2000, Dentaurum) combined with Omega 900 ceramic (Vita Zahnfabrik).

Material And Method: Eleven cylindrical matrixes were made for each alloy, and the metallic portion was obtained with the lost wax casting technique with standardized waxing of 4mm of height and of 4mm of diameter. The ceramic was applied according to the manufacturer's recommendations with the aid of a teflon matrix that allowed its dimension to be standardized in the same size as the metallic portion.

Sealing evaluation of the cervical base in intracoronal bleaching.

Discoloration of non-vital teeth is an esthetic deficiency frequently requiring bleaching treatment. The purpose of this study was to evaluate in vitro the cervical base efficacy in order to prevent or to minimize the leakage along the root canal filling and into the dentinal tubules. Thirty-eight extracted single-root human teeth were used, which were biomechanically prepared, filled, and divided into three experimental groups: G1, a cervical base was applied (3 mm of thickness) below the cemento-enamel junction, with resin-modified glass-ionomer cement (Vitremer); G2, the base was done with glass-ionomer cement (Vidrion R); and G3 (Control), did not receive any material as base.