Novel bilayered zirconia systems using recycled 3Y-TZP for dental applications.

Objective: To synthesize bilayer zirconia systems based on commercial or recycled 3Y-TZP obtained from non-milled remnants and to compare their optical and mechanical properties before and after aging.

Methods: Bilayer zirconia samples were fabricated using either recycled 3Y-TZP (3Y-R/4Y and 3Y-R/5Y) or commercial powders (3Y/4Y and 3Y/5Y). Microstructure and phase composition were analyzed using ScanningElectronMicroscopy (SEM) and X-Ray Diffraction (XRD).

Experimental bilayer zirconia systems after aging: Mechanical, optical, and microstructural characterization.

Objectives: To characterize two experimental zirconia bilayer materials compared to their monolithic controls, before and after hydrothermal aging.

Methods: Commercial zirconia powders were utilized to fabricate two bilayer materials: 3Y-TZP+ 5Y-PSZ (3Y+5Y/BI) and 4Y-PSZ+ 5Y-PSZ (4Y+5Y/BI), alongside control groups 3Y-TZP (3Y/C), 4Y-PSZ (4Y/C), and 5Y-PSZ (5Y/C). Compacted specimens were sintered (1550 °C- 2 h, 3 °C/min), and half of them underwent hydrothermal aging (134 °C-20h, 2.

Crystallization by microwave energy: Effects on the survival probability of lithia-based glass ceramics.

This study evaluated the survival probabilities of two lithia-based glass-ceramics after final crystallization in a microwave furnace using conventional crystallization as a reference. Disc-shaped samples of a lithium silicate (LS, Celtra Duo) and a lithium disilicate (LD, e.max CAD) were prepared and divided into two groups according to the crystallization method (n = 30): microwave (M) or conventional furnaces (C).

Biomimetic Tissue Engineering Strategies for Craniofacial Applications.

Biomimetics is the science of imitating nature's designs and processes to create innovative solutions for various fields, including dentistry and craniofacial reconstruction. In these areas, biomimetics involves drawing inspiration from living organisms/systems to develop new materials, techniques, and devices that closely resemble natural tissue structures and enhance functionality. This field has successfully demonstrated its potential to revolutionize craniofacial procedures, significantly improving patient outcomes.

Effect of bioceramic inclusions on gel-cast aliphatic polymer membranes for bone tissue engineering applications: An in vitro study.

Background: Polylactic acid (PLA) has been extensively used in tissue engineering. However, poor mechanical properties and low cell affinity have limited its pertinence in load bearing bone tissue regeneration (BTR) devices.

Objective: Augmenting PLA with β-Tricalcium Phosphate (β-TCP), a calcium phosphate-based ceramic, could potentially improve its mechanical properties and enhance its osteogenic potential.

Maxillary sinus membrane perforation rate utilizing osseodensification-mediated transcrestal sinus floor elevation: A multicenter clinical study.

Purpose: This multicenter cross-sectional clinical study aimed to evaluate the membrane perforation rate during transcrestal sinus floor elevation (TSFE) using osseodensification (OD) burs and assess risk factors associated with the procedure.

Materials And Methods: This study was conducted in six centers, following ethical standards and approved by local committees. It included patients over 18 years old missing maxillary posterior teeth with crestal residual bone height (RBH) ≥2 and ≤6 mm.

Characterization of a hydrothermally aged experimental alumina-toughened zirconia composite.

Objectives: To assess the effects of different aging protocols on chemical, physical, and mechanical properties of an experimental ATZ composite compared to a zirconia.

Methods: Disc-shaped specimens were obtained through uniaxial pressing of commercial powders (Tosoh), ATZ comprised of 80%ZrO/20%AlO (TZ-3YS20AB) and 3Y-TZP (3Y-SBE). The specimens of each material were divided into different groups according to the aging protocol: immediate, autoclave aging and hydrothermal reactor aging.

Partial fixed dental prostheses fabricated using fiber-reinforced composite resin supported by short and extra-short implants: A case series.

Purpose: This study aimed to evaluate the 10-year outcomes of partial fixed dental prostheses (P-FDPs) fabricated using metal-free fiber-reinforced composite (FRC) resin frameworks veneered with composite resin and supported by short and extra-short implants.

Methods: This study included 28 patients with 38 FRC prostheses supported by 96 implants. Implant and prosthesis survival and success rates were evaluated using Kaplan-Meier analysis.

Development of ZTA (80% AlO/20% ZrO) pre-sintered blocks for milling in CAD/CAM systems.

The present work aims to develop a production method of pre-sintered zirconia-toughened-alumina (ZTA) composite blocks for machining in a computer-aided design and computer-aided manufacturing (CAD-CAM) system. The ZTA composite comprised of 80% AlO and 20% ZrO was synthesized, uniaxially and isostatically pressed to generate machinable CAD-CAM blocks. Fourteen green-body blocks were prepared and pre-sintered at 1000 °C.

Sustained Release of Salicylic Acid for Halting Peri-Implantitis Progression in Healthy and Hyperglycemic Systemic Conditions: A Gottingen Minipig Model.

To develop a peri-implantitis model in a Gottingen minipig and evaluate the effect of local application of salicylic acid poly(anhydride-ester) (SAPAE) on peri-implantitis progression in healthy, metabolic syndrome (MS), and type-2 diabetes mellitus (T2DM) subjects. Eighteen animals were allocated to three groups: (i) control, (ii) MS (diet for obesity induction), and (iii) T2DM (diet plus streptozotocin for T2DM induction). Maxillary and mandible premolars and first molar were extracted.

Osseointegration of implant surfaces in metabolic syndrome and type-2 diabetes mellitus.

This in vivo study evaluated the bone healing response around endosteal implants with varying surface topography/chemistry in a preclinical, large transitional model induced with metabolic syndrome (MS) and type-2 diabetes mellitus (T2DM). Fifteen Göttingen minipigs were randomly distributed into two groups: (i) control (normal diet, n = 5) and (ii) O/MS (cafeteria diet for obesity induction, n = 10). Following obesity induction, five minipigs from the obese/metabolic syndrome (O/MS) group were further allocated, randomly, into the third experimental group: (iii) T2DM (cafeteria diet + streptozotocin).

A Narrative Review on Polycrystalline Ceramics for Dental Applications and Proposed Update of a Classification System.

Dental zirconias have been broadly utilized in dentistry due to their high mechanical properties and biocompatibility. Although initially introduced in dentistry as an infrastructure material, the high rate of technical complications related to veneered porcelain has led to significant efforts to improve the optical properties of dental zirconias, allowing for its monolithic indication. Modifications in the composition, processing methods/parameters, and the increase in the yttrium content and cubic phase have been presented as viable options to improve zirconias' translucency.

Minimally processed recycled yttria-stabilized tetragonal zirconia for dental applications: Effect of sintering temperature on glass infiltration.

This study aimed to develop a recycling process for the remnants of milled 3Y-TZP and enhance their properties using glass infiltration. 3Y-TZP powder was gathered from the vacuum system of CAD-CAM milling equipment, calcined and sieved (x < 75 μm). One hundred twenty discs were fabricated and pre-sintered at 1000 °C/h.

Finishing technique effect on strength of zirconia-reinforced lithium silicate ceramic.

The aim of this study was to evaluate the effect of two finishing techniques, glazing or polishing, in comparison with the as-cut condition, on the biaxial-flexural-strength (BFS) of a zirconia-reinforced lithium silicate ceramic (ZLS). Cylinders were milled from CAD/CAM blocks and sliced to obtain disc-shaped specimens (ISO6872:2015). Polished and glazed specimens were processed following the manufacturer's instructions.

Influence of abrasive dentifrices on polymeric reconstructive material properties after simulated toothbrushing.

To assess the influence of dentifrices with different abrasiveness levels on the properties of dental reconstructive materials. Forty-eight cylinders were obtained from four polymeric materials, being two CAD/CAM acrylic resins (Ivotion-Dent and Ivotion-Base), one injected acrylic resin (IvoBase-Hydrid) and one light-cured resin composite (Empress Direct). Specimens were allocated to four subgroups for toothbrushing simulation according to the dentifrice relative dentin abrasivity (RDA) and silica content: (i) RDA 0 = 0%; (ii) RDA 50 = 3%; (iii) RDA 100 = 10%; and (iv) RDA 120 = 25%.

Alumina-toughened zirconia nanocomposite: Aging effect on microstructural, optical, and mechanical properties.

Objectives: To process an alumina-toughened zirconia (ATZ) nanocomposite and to characterize its crystalline phases, microstructure, residual stress, mechanical and optical properties before and after two different artificial aging methodologies.

Methods: Disc-shaped specimens were obtained through uniaxial pressing of a commercial ATZ powder comprised of 80%ZrO / 20%AlO, with a particle size of 50 nm and 150 nm, respectively. Sintering was performed at 1500ºC for 2 h.

Hydrofluoric acid concentration and etching time affect differently the microstructure and surface properties of pressed lithium disilicate glass ceramics.

Objective: To evaluate the effect of different hydrofluoric acid concentrations and etching times on the surface, chemical composition and microstructure of lithium disilicate.

Material And Methods: Ninety specimens of pressed lithium disilicate (LDS) were obtained (IPS e.max Press, Rosetta SP and LiSi Press).

Reliability and Failure Mode of Ti-Base Abutments Supported by Narrow/Wide Implant Systems.

To assess the reliability and failure modes of Ti-base abutments supported by narrow and wide-diameter implant systems. Narrow (Ø3.5 × 10 mm) and wide (Ø5 × 10 mm) implant systems of two different manufacturers with internal conical connections (16°) and their respective Ti-base abutments (3.

In vitro assessment of the effect of luting agents, abutment height, and fatigue on the retention of zirconia crowns luted to titanium base implant abutments.

Statement Of Problem: The bonding of implant-supported prostheses is determined by abutment material, convergence angle, height, surface treatment, and luting agents. However, studies evaluating the bonding of luting agents to titanium base abutments with different heights under fatigue conditions are scarce.

Purpose: The purpose of this in vitro study was to evaluate the retention of zirconia crowns bonded with different luting agents to titanium base abutments of different heights before and after fatigue testing.

Ultrathin lithium disilicate and translucent zirconia crowns for posterior teeth: Survival and failure modes.

Purpose: To evaluate the reliability and failure modes of ultrathin (0.5 mm) lithium disilicate, translucent and ultra-translucent zirconia crowns for posterior teeth restorations.

Materials And Methods: Fifty-four mandibular first molar crowns of three ceramic materials: (1) Lithium disilicate (e.

Bone Tissue Engineering (BTE) of the Craniofacial Skeleton, Part I: Evolution and Optimization of 3D-Printed Scaffolds for Repair of Defects.

Bone tissue regeneration is a complex process that proceeds along the well-established wound healing pathway of hemostasis, inflammation, proliferation, and remodeling. Recently, tissue engineering efforts have focused on the application of biological and technological principles for the development of soft and hard tissue substitutes. Aim is directed towards boosting pathways of the healing process to restore form and function of tissue deficits.

Bone Tissue Engineering (BTE) of the Craniofacial Skeleton, Part II: Translational Potential of 3D-Printed Scaffolds for Defect Repair.

Computer-aided design/computer-aided manufacturing and 3-dimensional (3D) printing techniques have revolutionized the approach to bone tissue engineering for the repair of craniomaxillofacial skeletal defects. Ample research has been performed to gain a fundamental understanding of the optimal 3D-printed scaffold design and composition to facilitate appropriate bone formation and healing. Benchtop and preclinical, small animal model testing of 3D-printed bioactive ceramic scaffolds augmented with pharmacological/biological agents have yielded promising results given their potential combined osteogenic and osteoinductive capacity.

Evaluation of Implant Surface Modification with Nanohydroxyapatite Associated with the Use of L-PRF: In Vivo Study in Rats.

Leukocyte-platelet-rich fibrin (L-PRF) contains growth factors that stimulate bone regeneration. This study evaluated the bone repair in a tibia rat model around two implant surfaces in combination or not with L-PRF by assessing microtomographic and histomorphometric parameters. A total of 48 female rats were used in the study, in which 24 received implants with two types of surface treatments (dual acid etched-DAE or nanohydroxyapatite-nanoHA), and the other 24 received the same mini implants with L-PRF, which was collected by cardiac puncture, centrifugated, and inserted in the bone bed.

Osteogenic differentiation and reconstruction of mandible defects using a novel resorbable membrane: An in vitro and in vivo experimental study.

To evaluate the cellular response of both an intact fish skin membrane and a porcine-derived collagen membrane and investigate the bone healing response of these membranes using a translational, preclinical, guided-bone regeneration (GBR) canine model. Two different naturally sourced membranes were evaluated in this study: (i) an intact fish skin membrane (Kerecis Oral®, Kerecis) and (ii) a porcine derived collagen (Mucograft®, Geistlich) membrane, positive control. For the in vitro experiments, human osteoprogenitor (hOP) cells were used to assess the cellular viability and proliferation at 24, 48, 72, and 168 h.