The Effect of Temper Condition and Feeding Speed on the Additive Manufacturing of AA2011 Parts Using Friction Stir Deposition.

In the current study, solid-state additive manufacturing (SSAM) of two temper conditions AA2011 was successfully conducted using the friction stir deposition (FSD) process. The AA2011-T6 and AA2011-O consumable bars of 20 mm diameter were used as a feeding material against AA5083 substrate. The effect of the rotation rate and feeding speed of the consumable bars on the macrostructure, microstructure, and hardness of the friction stir deposited (FSD) materials were examined.

The Applicability of Die Cast A356 Alloy to Additive Friction Stir Deposition at Various Feeding Speeds.

In the current investigation, additive friction stir-deposition (AFS-D) of as-cast hypoeutectic A356 Al alloy was conducted. The effect of feeding speeds of 3, 4, and 5 mm/min at a constant rotational speed of 1200 rpm on the macrostructure, microstructure, and hardness of the additive manufacturing parts (AMPs) was investigated. Various techniques (OM, SEM, and XRD) were used to evaluate grain microstructure, presence phases, and intermetallics for the as-cast material and the AMPs.