In vitro aging of a heat/pressure-cured composite.

Specimens of a heat/pressure-cured microfill composite were aged in saline or distilled water at 37 degrees C up to 12 mon to determine if the flexure strength was affected by the aging media. No significant difference in the flexure strength was observed between the controls and the 12 mon aged specimens. Cyclic testing in distilled water resulted in a lower flexure strength at fracture than that observed for the aged specimens.

Surface roughness of polished amalgams.

The purpose of this project was to determine the amalgam surface roughness following finishing and polishing procedures. Nine high-copper amalgams were tested. They were hand-condensed in a 3 x 3 x 30 mm mold.