Debonding mechanism of zirconia and lithium disilicate resin cemented to dentin.

To evaluate debonding mechanism of zirconia and lithium disilicate cemented to dentin mimicking what could occur in a clinical setting. A null hypothesis of no difference in tensile bond strength between groups of zirconia and lithium disilicate cemented with resin cements was also tested. Zirconia rods ( = 100) were randomly assigned to two different surface treatment groups; air borne particle abrasion and hot etching by potassium hydrogen difluoride (KHF).

Effects of L-citrulline supplementation on heat stress physiology, lactation performance and subsequent reproductive performance of sows in summer.

Lactating sows are susceptible to heat stress (HS). Part of the thermoregulatory response to HS is to increase peripheral blood flow, which is mediated in part by the vasodilator, nitric oxide (NO). Therefore, the aim of this experiment was to determine the effect of supplementation of L-citrulline, a NO precursor, on symptoms of HS, lactation performance and subsequent reproductive performance of sows in summer.

A novel etching technique for surface treatment of zirconia ceramics to improve adhesion of resin-based luting cements.

Bonding of zirconia crowns and bridges to abutments is important, not only bonding of the thin resin layer to the abutment, but also bonding to the zirconia ceramic is crucial. Both mechanical and chemical adhesion are desired. Mechanical retention of dental porcelain achieved by etching with moderately concentrated hydrofluoric acid is not possible with zirconia ceramics.

Biological and physicochemical properties of carbon-graphite fibre-reinforced polymers intended for implant suprastructures.

The aim of this study was to determine water sorption, water solubility, dimensional change caused by water storage, residual monomers, and possible cytotoxic effects of heat-polymerized carbon-graphite fibre-reinforced composites with different fibre loadings based on methyl methacrylate/poly(methyl methacrylate) (MMA/PMMA) and the copolymer poly (vinyl chloride-co-vinyl acetate). Two different resin systems were used. Resin A contained ethylene glycol dimethacrylate (EGDMA) and 1,4-butanediol dimethacrylate (1,4-BDMA); the cross-linker in Resin B was diethylene glycol dimethacrylate (DEGDMA).

Permeability of different types of medical protective gloves to acrylic monomers.

Dental personnel and orthopedic surgeons are at risk when manually handling products containing methyl methacrylate (MMA). Dental products may also contain cross-linking agents such as ethylene glycol dimethacrylate (EGDMA) or 1,4-butanediol dimethacrylate (1,4-BDMA). Skin contact with monomers can cause hand eczema, and the protection given by gloves manufactured from different types of material is not well known.