Green Composites from Partially Bio-Based Poly(butylene succinate--adipate)-PBSA and Short Hemp Fibers with Itaconic Acid-Derived Compatibilizers and Plasticizers.

In this work, green composites have been developed and characterized using a bio-based polymeric matrix such as BioPBSA and the introduction of 30 wt.% short hemp fibers as a natural reinforcement to obtain materials with maximum environmental efficiency. In order to increase the interfacial adhesion between the matrix and the fiber to obtain better properties in the composites, a reactive extrusion process has been carried out.

Development and Characterization of High Environmentally Friendly Composites of Bio-Based Polyamide 1010 with Enhanced Fire Retardancy Properties by Expandable Graphite.

Bio-based polyamide 1010 was melt-compounded with different percentages (2.5 to 10.0 wt.

The Effect of Varying the Amount of Short Hemp Fibers on Mechanical and Thermal Properties of Wood-Plastic Composites from Biobased Polyethylene Processed by Injection Molding.

Biobased HDPE (bioHDPE) was melt-compounded with different percentages (2.5 to 40.0 wt.

Blood Hemoglobin Substantially Modulates the Impact of Gender, Morbid Obesity, and Hyperglycemia on COVID-19 Death Risk: A Multicenter Study in Italy and Spain.

Background: Hyperglycemia and obesity are associated with a worse prognosis in subjects with COVID-19 independently. Their interaction as well as the potential modulating effects of additional confounding factors is poorly known. Therefore, we aimed to identify and evaluate confounding factors affecting the prognostic value of obesity and hyperglycemia in relation to mortality and admission to the intensive care unit (ICU) due to COVID-19.

Development and Characterization of Environmentally Friendly Wood Plastic Composites from Biobased Polyethylene and Short Natural Fibers Processed by Injection Moulding.

Environmentally friendly wood plastic composites (WPC) with biobased high density polyethylene (BioHDPE) as the polymer matrix and hemp, flax and jute short fibers as natural reinforcements, were melt-compounded using twin-screw extrusion and shaped into pieces by injection molding. Polyethylene-graft-maleic anhydride (PE-g-MA) was added at two parts per hundred resin to the WPC during the extrusion process in order to reduce the lack in compatibility between the lignocellulosic fibers and the non-polar polymer matrix. The results revealed a remarkable improvement of the mechanical properties with the combination of natural fibers, along with PE-g-MA, highly improved stiffness and mechanical properties of neat BioHDPE.