Conventional sintering of nano-crystalline Yttria-Stabilized Zirconia enables high-strength, highly translucent and opalescent dental ceramics.

Development of restorative materials capable of mimicking optical and mechanical performance of natural teeth is a quest in aesthetic density. Yttria-Stabilized Zirconia (YSZ) ceramics represent one of the most popular choices for dental restorations, owing to their biocompatibility, white colour, and the possibility to use CAD-CAM technologies. In particular, YSZ doped with 3 mol.

Aging resistance, mechanical properties and translucency of different yttria-stabilized zirconia ceramics for monolithic dental crown applications.

Objectives: The dental market moves towards high-translucency monolithic zirconia dental crowns, which are usually placed either with - or without - a thin glaze layer. The microstructural features and the mechanical performances of these materials are still controversial, as well as their susceptibility to aging. This paper aims at studying these aspects in the current generation of zirconia dental crowns showing different degrees of translucency.

Surface roughened zirconia: towards hydrothermal stability.

Surface roughness is needed in several yttria-stabilized zirconia components used in restorative dentistry for osseointegration or adhesion purposes. This can be achieved by different treatments, which may also modify the microstructure of the surface. Among them, sandblasting and chemical etching are widely used, but their effect on hydrothermal aging of zirconia is not fully understood.

Enhanced reliability of yttria-stabilized zirconia for dental applications.

An increasing number of dental applications based on yttria-stabilized zirconia (3 Y-TZP) have been developed in recent years as a result of the advances and versatility of dry-processing and soft machining at the pre-sintered state. Nonetheless, the long-term surface stability of these materials in humid environment is still a matter of concern and may limit its application. In this work, a simple method to prevent hydrothermal degradation on the zirconia surface is studied in detail.