Ballistic Behavior of Bioinspired Nacre-like Composites.

In this paper, the ballistic performance of a multilayered composite inspired by the structural characteristics of nacre is numerically investigated using finite element (FE) simulations. Nacre is a natural composite material found in the shells of some marine mollusks, which has remarkable toughness due to its hierarchical layered structure. The bioinspired nacre-like composites investigated here were made of five wavy aluminum alloy 7075-T651 (AA7075) layers composed of ~1.

Tensile Behavior of 3D Printed Polylactic Acid (PLA) Based Composites Reinforced with Natural Fiber.

Natural fiber-reinforced composite (NFRC) filaments for 3D printing were fabricated using polylactic acid (PLA) reinforced with 1-5 wt% henequen flour comprising particles with sizes between 90-250 μm. The flour was obtained from natural henequen fibers. NFRCs and pristine PLA specimens were printed with a 0° raster angle for tension tests.

Mechanical Properties of Natural Fiber Reinforced Foamed Concrete.

The mechanical characterization of plain foamed concrete (PFC) and fiber-reinforced foamed concrete (FRFC) with a density of 700 kg/m was performed with compression and tension tests. FRFC was reinforced with the natural fiber henequen (untreated or alkaline-treated) at volume fractions of 0.5%, 1% and 1.

Shaking Table Test of U-Shaped Walls Made of Fiber-Reinforced Foamed Concrete.

Fiber-reinforced foamed concrete (FRFC) is a lightweight material that has the potential to perform well in seismic applications due to its low density and improved mechanical properties. However, studies focused on the seismic assessment of this material are limited. In this work, U-shaped wall specimens, made of FRFC reinforced with henequen fibers and plain foamed concrete (PFC) with a density of 900 kg/m, were subjected to shaking table tests.

Study of the porosity of calcified chicken eggshell using atomic force microscopy and image processing.

In this work, the porosity of the layers of calcified chicken eggshell (vertical crystal layer VCL, palisade layer PL and mammillary layer ML) was evaluated using atomic force microscopy (AFM) and image processing (IP). AFM topographic images were obtained from different locations for each layer and along the cross-section of calcified eggshell. Roughness parameters, surface area values, pore size and shape, surface porosity, area occupied by pores and pore density were obtained from AFM and IP.