Rechargeable-battery chemistry based on lithium oxide growth through nitrate anion redox.

Next-generation lithium-battery cathodes often involve the growth of lithium-rich phases, which enable specific capacities that are 2-3 times higher than insertion cathode materials, such as lithium cobalt oxide. Here, we investigated battery chemistry previously deemed irreversible in which lithium oxide, a lithium-rich phase, grows through the reduction of the nitrate anion in a lithium nitrate-based molten salt at 150 °C. Using a suite of independent characterization techniques, we demonstrated that a Ni nanoparticle catalyst enables the reversible growth and dissolution of micrometre-sized lithium oxide crystals through the effective catalysis of nitrate reduction and nitrite oxidation, which results in high cathode areal capacities (~12 mAh cm).

A Molten Salt Lithium-Oxygen Battery.

Despite the promise of extremely high theoretical capacity (2Li + O2 ↔ Li2O2, 1675 mAh per gram of oxygen), many challenges currently impede development of Li/O2 battery technology. Finding suitable electrode and electrolyte materials remains the most elusive challenge to date. A radical new approach is to replace volatile, unstable and air-intolerant organic electrolytes common to prior research in the field with alkali metal nitrate molten salt electrolytes and operate the battery above the liquidus temperature (>80 °C).

Controlled, Stepwise Reduction and Band Gap Manipulation of Graphene Oxide.

Graphene oxide (GO) has drawn tremendous interest as a tunable precursor in numerous areas, due to its readily manipulable surface. However, its inhomogeneous and nonstoichiometric structure makes achieving chemical control a major challenge. Here, we present a room-temperature based, controlled method for the stepwise reduction of GO, with evidence of sequential removal of each organic moiety.