Dendrite initiation and propagation in lithium metal solid-state batteries.

All-solid-state batteries with a Li anode and ceramic electrolyte have the potential to deliver a step change in performance compared with today's Li-ion batteries. However, Li dendrites (filaments) form on charging at practical rates and penetrate the ceramic electrolyte, leading to short circuit and cell failure. Previous models of dendrite penetration have generally focused on a single process for dendrite initiation and propagation, with Li driving the crack at its tip.

Temperature Dependence of Lithium Anode Voiding in Argyrodite Solid-State Batteries.

Void formation at the Li/ceramic electrolyte interface of an all-solid-state battery on discharge results in high local current densities, dendrites on charge, and cell failure. Here, we show that such voiding is reduced at the Li/LiPSCl interface at elevated temperatures, sufficient to increase the critical current before voiding and cell failure from <0.25 mA cm at 25 °C to 0.

Visualizing plating-induced cracking in lithium-anode solid-electrolyte cells.

Lithium dendrite (filament) propagation through ceramic electrolytes, leading to short circuits at high rates of charge, is one of the greatest barriers to realizing high-energy-density all-solid-state lithium-anode batteries. Utilizing in situ X-ray computed tomography coupled with spatially mapped X-ray diffraction, the propagation of cracks and the propagation of lithium dendrites through the solid electrolyte have been tracked in a Li/LiPSCl/Li cell as a function of the charge passed. On plating, cracking initiates with spallation, conical 'pothole'-like cracks that form in the ceramic electrolyte near the surface with the plated electrode.