Studying the Plastic Deformation of Cu-Ti-C-B Composites in a Favorable Stress State.

Composites with a copper matrix attract the attention of researchers due to their ability to combine high ductility, heat conductivity, and electrical conductivity of the matrix with the high hardness and strength of the reinforcing phases. In this paper, we present the results of studying the effect of thermal deformation processing of a Сu-Ti-C-B composite produced by self-propagating high-temperature synthesis (SHS) on its ability to deform plastically without failure. The composite consists of a copper matrix and reinforced particles of titanium carbide TiC (sized up to 1.

The Effect of the Stress State, Testing Temperature, and Hardener Composition on the Strength of an AlMg5/Epoxy Metal-Polymer Joint.

The regularities of the effect of a complex stress state on the strength of an AlMg5/epoxy adhesive joint are experimentally studied at -50 and +23 °C in tension+shear and compression+shear tests with different normal-to-shear stress ratios. The tests use modified Arcan specimens and Brazil-nut-sandwich specimens, with the lateral faces of the adhesive layer having a shape of a mushroom-like "ridge" aimed at reducing stress concentration at the specimen edges. An original computational model of a selected microvolume including the interface together with the adjacent substrate and adhesive layers is used to process the experimental results.