Reversing the training effect in exchange biased CoO/Co bilayers.

We performed a detailed study of the training effect in exchange biased CoO/Co bilayers. High-resolution measurements of the anisotropic magnetoresistance (AMR) display an asymmetry in the first magnetization reversal process and training in the subsequent reversal processes. Surprisingly, the AMR measurements as well as magnetization measurements reveal that it is possible to partially reinduce the untrained state by performing a hysteresis measurement with an in-plane external field perpendicular to the cooling field.

Positive domain wall resistance of 180 degrees Néel walls in Co thin films.

We measured the intrinsic domain wall resistance (DWR) of 180 degrees Ne el walls in a polycrystalline Co thin film deposited on top of a patterned antiferromagnetic CoO template. After field cooling through the CoO blocking temperature, exchange bias induces a spatially modulated coercivity of the Co film, resulting in a periodic domain pattern with 180 degrees Ne el walls. The intrinsic DWR is determined unambiguously by using rotating magnetic fields that result in a reversible creation and annihilation of the Ne el walls.