Sulfuric acid baking and leaching of spent Co-Mo/Al2O3 catalyst.

Dissolution of metals from a pre-oxidized refinery plant spent Co-Mo/Al(2)O(3) catalyst have been tried through low temperature (200-450 degrees C) sulfuric acid baking followed by mild leaching process. Direct sulfuric acid leaching of the same sample, resulted poor Al and Mo recoveries, whereas leaching after sulfuric acid baking significantly improved the recoveries of above two metals. The pre-oxidized spent catalyst, obtained from a Korean refinery plant found to contain 40% Al, 9.

An overview on the production of pigment grade titania from titania-rich slag.

To recover pigment grade TiO2, operating plants all over the world use chemical processes. Slag-based technology is considered to be attractive because of low waste generation and low chemical cost due to high titanium content and is poised to replace the conventional technology. This paper provides a review of the slag-based technology with the specific aim to produce leachable slag and achieving high titania yield from recovered wastes.