Measurement of the surface-enhanced coherent anti-Stokes Raman scattering (SECARS) due to the 1574 cm(-1) surface-enhanced Raman scattering (SERS) mode of benzenethiol using low-power (<20 mW) CW diode lasers.

The surface-enhanced coherent anti-Stokes Raman scattering (SECARS) from a self-assembled monolayer (SAM) of benzenethiol on a silver-coated surface-enhanced Raman scattering (SERS) substrate has been measured for the 1574 cm(-1) SERS mode. A value of 9.6 ± 1.

Measurement of the Raman line widths of neat benzenethiol and a self-assembled monolayer (SAM) of benzenethiol on a silver-coated surface-enhanced Raman scattering (SERS) substrate.

Raman line widths of neat benzenethiol and a self-assembled monolayer (SAM) of benzenethiol on a surface-enhanced Raman scattering (SERS) substrate have been measured using a mini spectrometer with a resolution (full width at half-maximum) of 3.3 ± 0.2 cm(-1).

Growth of highly oriented ZnO nanowires on GaN substrates for electronic and optical sensor applications.

In this Paper we present growth and characterization results of highly oriented ZnO nanowires grown on wide bandgap GaN substrates. Experimental results on the ZnO nanowires grown on p-GaN are presented with growth morphology and dimensionality control. We also present experimental results on these nanowire arrays such as I-V measurements and UV sensitivity measurements.

Gigantic enhancement in response and reset time of ZnO UV nanosensor by utilizing Schottky contact and surface functionalization.

UV response of ZnO nanowire nanosensor has been studied under ambient condition. By utilizing Schottky contact instead of Ohmic contact in device fabrication, the UV sensitivity of the nanosensor has been improved by four orders of magnitude, and the reset time has been drastically reduced from approximately 417 to approximately 0.8 s.

Patterned growth of horizontal ZnO nanowire arrays.

We report an approach to fabricating patterned horizontal ZnO nanowire arrays with a high degree of control over their dimensionality, orientation, and uniformity. Our method combines electron beam lithography and a low temperature hydrothermal decomposition. This approach opens up possibilities to fabricate ZnO NW array based strain and force sensors, two-dimensional photonic crystals, integrated circuit interconnects, and alternative current nanogenerators.