Amphiphilic, thixotropic additives for extrusion-based 3D printing of silica-reinforced silicone.

The ability to utilize extrusion-based, direct ink write (DIW) 3D printing to create silica-reinforced silicones with complex structures could expand their utility in industrial and biomedical applications. Sylgard 184, a common Pt-cure silicone, lacks the thixotropic behavior necessary for effective printing and its hydrophobicity renders cured structures susceptible to biofouling. Herein, we evaluated the efficacy of various PEO-silane amphiphiles (PEO-SAs) as thixotropic and surface modifying additives in Sylgard 184.

Luminescence in Ce(IV) polyoxometalate [Ce(W5O18)2]8-: a combined experimental and theoretical study.

Herein we describe the unique luminescent behavior observed in [Ce(IV)(W(5)O(18))(2)](8-) clusters and examine the photophysical properties using density functional theory.

A combinatorial approach to studying the effects of N-alkyl groups on poly(N-alkyl and N,N-dialkylacrylamide) solubility.

Soluble polymers including poly(N-alkylacrylamide)s with low mole percent loadings of pendant groups are of interest in applications in catalysis, synthesis, sequestration, and soluble affinity chromatography where their thermal and phase-dependent solubility facilitates purification and separation. This work describes a library synthesis and study of the effects of polymer composition on the phase-selective solubility of dye-labeled poly(N-n-octadecylacrylamide-co-N-n-butylacrylamide) copolymers. To study the relative importance of n-octadecyl versus n-butyl groups, copolymers with different ratios of n-octadecylacrylamide and n-butylacrylamide but with similar degrees of polymerization and polydispersity were prepared by a split-pool synthesis using a highly soluble poly(N-acryloxy-2-dodecylsuccinimide) as the precursor.