Beneficial Effects of Ethyl-Cyanoacrylate Coating Against Candida Albicans Biofilm Formation.

The aim of this study was to verify whether modifications made in a hard chairside reline resin by an ethyl-cyanoacrylate adhesive, ECA (Super Bonder®, Loctite, Itapevi, SP, Brazil) would be able to inhibit or reduce Candida albicans biofilm formation on its surface, comparing to a commercial surface sealant (BisCover®, Bisco, Schaumburg, USA). Reline resin specimens were fabricated and randomly divided into 6 groups (n=8): CG (control group), no surface treatment; ECA1, ECA coating on the surface before sterilization; ECA2, ECA coating after sterilization; ECA3, ECA incorporated in the resin bulk; DPE1, BisCover® coating before sterilization; DPE2, BisCover® coating after sterilization. Specimens were inoculated with C.

Effect of potentially chromogenic beverages on shear bond strength of acrylic denture teeth to heat-polymerized denture base resins.

Background: Detachment of denture acrylic resin artificial teeth from denture base resin is one of the most common problems presented by denture wearers.

Purpose: This study investigated the shear bond strength (SBS) and fracture type of bonding interface of two commercial acrylic teeth (Vipi Dent Plus e Biolux) to two denture base resins (Vipi Cril e Lucitone 550) after immersion in potentially chromogenic beverages (coffee, cola soft drink, and red wine) or control solution (distilled water).

Materials And Methods: Maxillary central incisor acrylic teeth were placed at 45° to denture base resin and submitted to short polymerization cycle according to manufacturers.

Antifungal activity of 4% chlorhexidine and 2% sodium hypochlorite against Candida albicans biofilms.

The purpose of this study was to determine the antifungal efficacy of 4% chlorhexidine (CHX) and 2% sodium hypochlorite (NaOCl) on 24-hour Candida albicans biofilms. Candida albicans biofilms were developed on acrylic resin specimens, which were randomly assigned to 1 of 5 groups (n = 3 per group) exposed to 1 mL of 4% CHX for 2, 4, 6, 8, or 10 minutes. Biofilms in contact with 1 mL of distilled water or 2% NaOCl for 10 minutes were used as positive and negative controls (n = 3 per group), respectively.