Enhanced Adsorption of Epoxy-Functional Nanoparticles onto Stainless Steel Significantly Reduces Friction in Tribological Studies.

Epoxy-functional sterically-stabilized diblock copolymer nanoparticles (ca. 27 nm) are prepared via RAFT dispersion polymerization in mineral oil. Nanoparticle adsorption onto stainless steel is examined using a quartz crystal microbalance.

Tuning the Glass Transition Temperature of a Core-Forming Block during Polymerization-Induced Self-Assembly: Statistical Copolymerization of Lauryl Methacrylate with Methyl Methacrylate Provides Access to Spheres, Worms, and Vesicles.

A series of poly(lauryl methacrylate)-poly(methyl methacrylate--lauryl methacrylate) (PLMA -P(MMA--LMA) ) diblock copolymer nanoparticles were synthesized via RAFT dispersion copolymerization of 90 mol % methyl methacrylate (MMA) with 10 mol % lauryl methacrylate (LMA) in mineral oil by using a poly(lauryl methacrylate) (PLMA) precursor with a mean degree of polymerization (DP) of either 22 or 41. H NMR studies of the copolymerization kinetics suggested an overall comonomer conversion of 94% within 2.5 h.

Time-resolved small-angle neutron scattering studies of the thermally-induced exchange of copolymer chains between spherical diblock copolymer nanoparticles prepared via polymerization-induced self-assembly.

Sterically-stabilized diblock copolymer nanoparticles (a.k.a.

Is Carbon Black a Suitable Model Colloidal Substrate for Diesel Soot?

Soot formation in diesel engines is known to cause premature engine wear. Unfortunately, genuine diesel soot is expensive to generate, so carbon blacks are often used as diesel soot mimics. Herein, the suitability of a commercial carbon black (Regal 250R) as a surrogate for diesel soot dispersed in engine base oil is examined in the presence of two commonly used polymeric lubricant additives.

Determination of Effective Particle Density for Sterically Stabilized Carbon Black Particles: Effect of Diblock Copolymer Stabilizer Composition.

Two poly(styrene-b-hydrogenated isoprene) (PS-PEP) copolymers and a poly(styrene-b-hydrogenated butadiene) (PS-PB) diblock copolymer of differing polystyrene content (20, 28 or 35 mol %) and molecular weight (117-183 kg mol(-1)) are examined. These copolymers form star-like micelles in n-dodecane, as judged by TEM, DLS, and SAXS studies. At ambient temperature, such micelles are known to adsorb intact onto a model colloidal substrate such as carbon black, conferring a high degree of dispersion (Growney, D.

Microgel colloidosomes based on pH-responsive poly(tert-butylaminoethyl methacrylate) latexes.

Emulsion copolymerization of 2-(tert-butylamino)ethyl methacrylate (TBAEMA) with divinylbenzene (DVB) cross-linker in the presence of monomethoxy-capped poly(ethylene glycol) methacrylate (PEGMA) at 70 °C afforded sterically stabilized poly[2-(tert-butylamino)ethyl methacrylate] (PTBAEMA) latexes at 10% solids at pH 9. Such particles proved to be an effective Pickering emulsifier at pH 10 for both n-dodecane and n-hexane. (1)H NMR spectroscopy was used to follow the model reaction between the secondary amine of the TBAEMA monomer and the isocyanate groups of tolylene 2,4-diisocyanate-terminated poly(propylene glycol) (PPG-TDI).

Micellization and adsorption behavior of a near-monodisperse polystyrene-based diblock copolymer in nonpolar media.

The micellar self-assembly behavior of a near-monodisperse polystyrene-hydrogenated polyisoprene (PS-PEP) diblock copolymer is examined in non-polar media (either n-heptane or n-dodecane). Direct dissolution of this diblock copolymer leads to the formation of relatively large polydisperse colloidal aggregates that are kinetically frozen artifacts of the solid-state copolymer morphology. Dynamic light scattering (DLS) and transmission electron microscopy studies indicate that heating such copolymer dispersions up to 90-110 °C leads to a structural rearrangement, with the generation of relatively small, well-defined spherical micelles that persist on cooling to 20 °C.