The Effect of Surface Chemistry on the Glass Transition of Polycarbonate Inside Cylindrical Nanopores.

The effect of surface chemistry on the glass transition of polycarbonate (PC) inside cylindrical nanopores is studied. Polycarbonate is melt-wetted into nanoporous anodic aluminum oxide (AAO) treated with hydrophobic alkyl- and fluorosilanes of varying length. The curvature observed at the nanowire tips is consistent with a contact angle descriptive of polycarbonate-AAO surface interactions.

The effect of nanoparticle location and shape on thermal transitions observed in hydrated layer-by-layer assemblies.

Nanoparticles can have a profound effect on thermal transitions observed in polymer nanocomposites. Many layer-by-layer (LbL) assemblies contain nanoparticles for added functionality, but the resulting effects of nanoparticles on an LbL film's thermal properties are not known. Previously, we have shown that a nanoparticle-free LbL film containing strong polyelectrolytes, poly(diallyldimethylammonium chloride)/poly(styrene sulfonate) (PDAC/PSS), exhibited a single reversible thermal transition much like a glass-melt transition.

In vivo whole animal fluorescence imaging of a microparticle-based oral vaccine containing (CuInSe(x)S(2-x))/ZnS core/shell quantum dots.

Zinc sulfide-coated copper indium sulfur selenide (CuInSexS2-x/ZnS core/shell) nanocrystals were synthesized with size-tunable red to near-infrared (NIR) fluorescence with high quantum yield (40%) in water. These nanocrystals were tested as an imaging agent to track a microparticle-based oral vaccine administered to mice. Poly(lactic-co-glycolic acid) (PLGA) microparticle-encapsulated CuInSexSe2-x/ZnS quantum dots were orally administered to mice and were found to provide a distinct visible fluorescent marker in the gastrointestinal tract of living mice.

A comparison of thermal transitions in dip- and spray-assisted layer-by-layer assemblies.

Spray-assisted layer-by-layer (LbL) assembly is far more rapid than conventional dip-assisted assembly methods and has gained widespread interest recently. Even so, it has remained unclear as to how the structure and properties of the resulting LbL film vary with processing method. Here, we compared the thermal properties of poly(ethylene oxide) (PEO)/poly(acrylic acid) (PAA) and PEO/poly(methacrylic acid) (PMAA) hydrogen-bonded LbL assemblies prepared using both dip-assisted and spray-assisted deposition methods.

CuInSe2 Quantum Dot Solar Cells with High Open-Circuit Voltage.

CuInSe2 (CISe) quantum dots (QDs) were synthesized with tunable size from less than 2 to 7 nm diameter. Nanocrystals were made using a secondary phosphine selenide as the Se source, which, compared to tertiary phosphine selenide precursors, was found to provide higher product yields and smaller nanocrystals that elicit quantum confinement with a size-dependent optical gap. Photovoltaic devices fabricated from spray-cast CISe QD films exhibited large, size-dependent, open-circuit voltages, up to 849 mV for absorber films with a 1.

Influence of composition on the performance of sintered Cu(In,Ga)Se2 nanocrystal thin-film photovoltaic devices.

Thin-film photovoltaic devices (PVs) were prepared by selenization using oleylamine-capped Cu(In,Ga)Se2 (CIGS) nanocrystals sintered at a high temperature (>500 °C) under Se vapor. The device performance varied significantly with [Ga]/[In+Ga] content in the nanocrystals. The highest power conversion efficiency (PCE) observed in the devices studied was 5.

Raman Spectroscopy of Oxide-Embedded and Ligand-Stabilized Silicon Nanocrystals.

Oxide-embedded and oxide-free alkyl-terminated silicon (Si) nanocrystals with diameters ranging from 3 nm to greater than 10 nm were studied by Raman spectroscopy. For ligand-passivated nanocrystals, the zone center Raman-active mode of diamond cubic Si shifted to lower frequency with decreasing size, accompanied by asymmetric peak broadening, as extensively reported in the literature. The size dependence of the Raman peak shifts, however, was significantly more pronounced than previously reported or predicted by the RWL (Richter, Wang, and Ley) and bond polarizability models.

Thickness-limited performance of CuInSe₂ nanocrystal photovoltaic devices.

This paper reports our latest results using colloidal CuInSe₂ nanocrystal inks to prepare photovoltaic (PV) devices. Thus far, devices with nanocrystal layers processed under ambient conditions with no post-deposition treatment have achieved power conversion efficiencies of up to 3.1%.