High temperature corrosion and oxide scale formation of nickel in molten NaOH at various basicity levels.

The corrosion behavior of alloy Ni 201 in molten sodium hydroxide (NaOH) at 600 °C was investigated at varying basicity levels of the molten NaOH. The ability for Ni 201 to form passivating oxides was investigated after immersion tests varying from 70 to 340 h under atmospheres of argon and argon with different partial pressure of water. Morphology and thicknesses of the corrosion products were characterized by Scanning Electron Microscopy (SEM) and crystallography of the corrosion products by X-ray Diffraction (XRD).