A commercially viable solution process to control long-chain branching in polyethylene.

In polyolefins, long-chain branching is introduced through an energy-intensive, high-pressure radical process to form low-density polyethylene (LDPE). In the current work, we demonstrated a ladder-like polyethylene architecture through solution polymerization of ethylene and less than 1 mole % of α,ω-dienes, using a dual-chain catalyst. The ladder-branching mechanism requires catalysts with two growing polymer chains on the same metal center, thus enchaining the diene without the requirement of a steady-state concentration of pendant vinyl groups.

Computational and Experimental Studies of Regioselective SAr Halide Exchange (Halex) Reactions of Pentachloropyridine.

The Halex reaction of pentachloropyridine with fluoride ion was studied experimentally and computationally with a modified ab initio G3MP2B3 method. The G3 procedure was altered, as the anionic transition state optimizations failed due to the lack of diffuse functions in the small 6-31G* basis set. Experimental Halex regioselectivities were consistent with kinetic control at the 4-position.

Penultimate effect in ethylene-styrene copolymerization and the discovery of highly active ethylene-styrene catalysts with increased styrene reactivity.

For the first time commercially relevant catalysts for the copolymerization of ethylene and styrene have been identified. The catalysts maintain very high copolymer efficiencies at relatively high reactor temperatures without sacrificing styrene comonomer reactivity. The observations which led to this discovery are based upon the kinetic analysis of ethylene-styrene copolymerization using constrained geometry catalyst (eta5-C5Me4)(SiMe2-N-t-Bu)TiMe2 (1).

Catalytic production of olefin block copolymers via chain shuttling polymerization.

We report a catalytic system that produces olefin block copolymers with alternating semicrystalline and amorphous segments, achieved by varying the ratio of alpha-olefin to ethylene in the two types of blocks. The system uses a chain shuttling agent to transfer growing chains between two distinct catalysts with different monomer selectivities in a single polymerization reactor. The block copolymers simultaneously have high melting temperatures and low glass transition temperatures, and therefore they maintain excellent elastomeric properties at high temperatures.