Laser Powder Bed Fusion Parameters Optimization for Enhanced Mechanical Properties of EOS Co-Cr Dental Alloy.

This research explores how variations in laser powder bed fusion (LPBF) parameters-laser power (), scanning speed (), and base plate preheating temperature ()-affect the mechanical properties of the EOS Co-Cr SP2 dental alloy. A central composite design (CCD) was used to optimize the process parameters. Mechanical testing focused on crucial properties for dental applications, including yield strength (), elongation (), toughness (), and flexural strength ().

Additively Manufactured Commercial Co-Cr Dental Alloys: Comparison of Microstructure and Mechanical Properties.

Laser-powder bed fusion (LPBF) is one of the preferred techniques for producing Co-Cr metal structures for dental prosthodontic appliances. However, there is generally insufficient information about material properties related to the production process and parameters. This study was conducted on samples produced from three different commercially available Co-Cr dental alloys produced on three different LPBF machines.

Femoral head wear and metallosis caused by damaged titanium porous coating after primary metal-on-polyethylene total hip arthroplasty: a case report.

Excessive metal femoral head wear has been described only as revision surgery complication after primary ceramic-on-ceramic total hip arthroplasty (THA). Here, we present the first case of metal femoral head wear after primary metal-on-polyethylene THA. A 56-year-old woman was referred to our outpatient clinic 17 years after primary right-sided THA, experiencing pain and decreased right hip range of motion.