Record-High-Performance Hydrogenated In-Ga-Zn-O Flexible Schottky Diodes.

High-performance In-Ga-Zn-O (IGZO) Schottky diodes (SDs) were fabricated using hydrogenated IGZO (IGZO:H) at a maximum process temperature of 150 °C. IGZO:H was prepared by Ar + O + H sputtering. IGZO:H SDs on a glass substrate exhibited superior electrical properties with a very high rectification ratio of 3.

Quantum Confinement Effect in Amorphous In-Ga-Zn-O Heterojunction Channels for Thin-Film Transistors.

Electrical and carrier transport properties in In-Ga-Zn-O thin-film transistors (IGZO TFTs) with a heterojunction channel were investigated. For the heterojunction IGZO channel, a high-In composition IGZO layer (IGZO-high-In) was deposited on a typical compositions IGZO layer (IGZO-111). From the optical properties and photoelectron yield spectroscopy measurements, the heterojunction channel was expected to have the type-II energy band diagram which possesses a conduction band offset (Δ) of ~0.

Memristive Characteristic of an Amorphous Ga-Sn-O Thin-Film Device with Double Layers of Different Oxygen Density.

We have found a memristive characteristic of an amorphous Ga-Sn-O (α-GTO) thin-film device with double layers of different oxygen density. The double layers are deposited using radio frequency (RF) magnetron sputtering, whose gas for the lower layer contains less oxygen, whereas that for the upper layer contains more oxygen, and it is assumed that the former contains more oxygen vacancies, whereas the latter contains fewer vacancies. The characteristic is explained by drift of oxygen and is stable without forming operation because additional structures such as filament are unnecessary.

Memristive characteristic of an amorphous Ga-Sn-O thin-film device.

We have found a memristive characteristic of an α-GTO thin-film device. The α-GTO thin-film layer is deposited using radio-frequency (RF) magnetron sputtering at room temperature and sandwiched between the Al top and bottom electrodes. It is found that the hysteresis loop of the flowing current (I) and applied voltage (V) characteristic becomes larger and stable after the one hundredth cycle.