Testing Protocol Development for the Fracture Toughness of Parts Built with Big Area Additive Manufacturing.

The mechanical testing of additively manufactured parts has largely relied on the existing standards developed for traditional manufacturing. While this approach leverages the investment made in current standards development, it inaccurately assumes that the mechanical response of additive manufacturing (AM) parts is identical to that of parts manufactured through traditional processes. When considering thermoplastic, material extrusion AM, the differences in response can be attributed to an AM part's inherent inhomogeneity caused by porosity, interlayer zones, and surface texture.

Direct Ink-Write Printing of Ceramic Clay with an Embedded Wireless Temperature and Relative Humidity Sensor.

This research presents a simple method to additively manufacture Cone 5 porcelain clay ceramics by using the direct ink-write (DIW) printing technique. DIW has allowed the application of extruding highly viscous ceramic materials with relatively high-quality and good mechanical properties, which additionally allows a freedom of design and the capability of manufacturing complex geometrical shapes. Clay particles were mixed with deionized (DI) water at different ratios, where the most suitable composition for 3D printing was observed at a 1:5 w/c ratio (16.

Electrical and Thermal Characterization of 3D Printed Thermoplastic Parts with Embedded Wires for High Current-Carrying Applications.

Fabrication of parts exhibiting multi-functionality has recently been complemented by hybrid polymer extrusion additive manufacturing in combination with wire embedding technology. While much mechanical characterization has been performed on parts produced with fused deposition modeling, limited characterization has been performed when combined electrical and thermal loads are applied to 3D printed multi-material parts. As such, this work describes the design, fabrication, and testing of 3D printed thermoplastic coupons containing embedded copper wires that carried current.