In Vitro Studies Regarding the Effect of Cellulose Acetate-Based Composite Coatings on the Functional Properties of the Biodegradable Mg3Nd Alloys.

Magnesium (Mg) alloys are adequate materials for orthopedic and maxilo-facial implants due to their biocompatibility, good mechanical properties closely related to the hard tissues, and processability. Their main drawbacks are the high-speed corrosion process and hydrogen release. In order to improve corrosion and mechanical properties, the Mg matrix can be strengthened through alloying elements with high temperature-dependent solubility materials.

Assessment of Microstructural, Mechanical and Electrochemical Properties of Ti-42Nb Alloy Manufactured by Electron Beam Melting.

The β-type Ti-42Nb alloy has been successfully manufactured from pre-alloyed powder using the E-PBF method for the first time. This study presents thorough microstructural investigations employing diverse methodologies such as EDS, XRD, TEM, and EBSD, while mechanical properties are assessed using UPT, nanoindentation, and compression tests. Microstructural analysis reveals that Ti-42Nb alloy primarily consisted of the β phase with the presence of a small amount of nano-sized α″-martensite formed upon fast cooling.

Effect of Fluoride Coatings on the Corrosion Behavior of Mg-Zn-Ca-Mn Alloys for Medical Application.

The most critical shortcoming of magnesium alloys from the point of view of medical devices is the high corrosion rate, which is not well-correlated with clinical needs. It is well- known that rapid degradation occurs when an implant made of Mg-based alloys is placed inside the human body. Consequently, the implant loses its mechanical properties and failure can occur even if it is not completely degraded.

Sulfonitrocarburizing of High-Speed Steel Cutting Tools: Kinetics and Performances.

The scholarly literature records information related to the performance increase of the cutting tools covered by the superficial layers formed "in situ" when applying thermochemical processing. In this context, information is frequently reported on the carbamide role in processes aiming carbon and nitrogen surface saturation. Sulfur, together with these elements adsorbed and diffused in the cutting tools superficial layers, undoubtedly ensures an increase of their operating sustainability.

Evaluation of the Behavior of Two CAD/CAM Fiber-Reinforced Composite Dental Materials by Immersion Tests.

Fiber-reinforced composites are used as restorative materials for prosthetic oral rehabilitation. Gastroesophageal reflux disease (GERD) is an accustomed affection with various oral manifestations. This study aimed to evaluate the behavior of two high-performance CAD/CAM milled reinforced composites (Trinia™, TriLor) in artificial saliva at different pH levels through immersion tests, and to determine if changes in mass or surface morphology at variable pH, specific for patients affected by GERD, appear.

The Effect of Disinfectants Absorption and Medical Decontamination on the Mechanical Performance of 3D-Printed ABS Parts.

Producing parts by 3D printing based on the material extrusion process determines the formation of air gaps within layers even at full infill density, while external pores can appear between adjacent layers making prints permeable. For the 3D-printed medical devices, this open porosity leads to the infiltration of disinfectant solutions and body fluids, which might pose safety issues. In this context, this research purpose is threefold.

Bending Fracture of Different Zirconia-Based Bioceramics for Dental Applications: A Comparative Study.

The fabrication of fixed dental prostheses using aesthetic materials has become routine in today's dentistry. In the present study, three-unit full zirconia fixed prosthetic restorations obtained by computer-aided design/computer-aided manufacturing (CAD/CAM) technology were tested by bending trials. The prostheses were intended to replace the first mandibular left molar and were manufactured from four different types of zirconia bioceramics (KatanaTM Zirconia HTML and KatanaTM Zirconia STML/Kuraray Noritake Dental Inc.

Experimental Study Regarding the Behavior at Different pH of Two Types of Co-Cr Alloys Used for Prosthetic Restorations.

Cobalt-chromium (Co-Cr) alloys are widely utilized in dentistry. The salivary pH is a significant factor, which affects the characteristics and the behavior of dental alloys through corrosion. This study aimed to evaluate the corrosion behavior in artificial saliva with different pH values (3, 5.

Mechanically Alloyed CoCrFeNiMo High-Entropy Alloy for Corrosion Resistance Coatings.

High-entropy alloys could provide a solution for corrosion resistance due to their impressive properties. Solid-state processing of high purity Co, Cr, Fe, Ni and Mo metallic powders and consolidation resulted in a bulk material that was further machined into electro spark deposition electrodes. After the stainless steel substrate surface preparation, thin successive layers of the high-entropy alloy were deposited and Pull-Off testing was performed on the newly obtained coating, for a better understanding of the adhesion efficiency of this technique.

Assessment of Force Retention between Milled Metallic and Ceramic Telescopic Crowns with Different Taper Angles Used for Oral Rehabilitation.

The present study assessed the retention forces corresponding to different telescopic systems used in removable prosthetic dentures. The telescopic systems were represented by Co-Cr alloy or zirconia-based primary crowns and Co-Cr secondary crowns. All crowns were manufactured using computer-aided design/computer-aided manufacturing technology (CAD/CAM).

Sputtered Si and Mg doped hydroxyapatite for biomedical applications.

Hydroxyapatite (HAP) coatings are applied on metallic implant materials to combine mechanical properties of metallic material with bioactivity abilities of HAP ceramic. In this study, HAP coatings with additions of Si and Mg are proposed to be deposited on Ti6Al4V substrates by RF magnetron sputtering. Chemical bonding, morphology, topography and corrosion resistance in simulated body fluids (SBF) of the coatings were investigated.

Characterization and In Vitro and In Vivo Assessment of a Novel Cellulose Acetate-Coated Mg-Based Alloy for Orthopedic Applications.

Despite their good biocompatibility and adequate mechanical behavior, the main limitation of Mg alloys might be their high degradation rates in a physiological environment. In this study, a novel Mg-based alloy exhibiting an elastic modulus E = 42 GPa, Mg-1Ca-0.2Mn-0.