Relative abrasive potential of silica-based conventional and tablet dentifrices on enamel and dentin.

Objectives: This in vitro study aimed to investigate the toothbrushing wear on both enamel and dentin surfaces of reference and commercially available dentifrices.

Methods: Bovine enamel and dentin blocks were initially polished and embedded within a resin composite in square shapes (10×8×6 mm3). Employing toothbrushes equipped with nylon bristles, a toothbrushing machine was utilized, subjecting dentin specimens (n = 36) to 500 brush cycles and enamel samples to 5000 brush cycles (n = 36).

A comprehensive study on MDP effects: Microshear bond strength and fatigue resistance in 4YSZ ceramics.

The aim of this study is to assess the presence of MDP at various stages of the bonding procedure, enhance the adhesive and mechanical behavior of cemented zirconia ceramics. Fifty ceramic slices (15 × 15 × 2 mm) and 48 discs (Ø= 10 mm, 1 mm thickness) were prepared, sintered, air-abraded with aluminum oxide, and allocated considering: 1) microshear bond strength (µSBS) between ceramic slices and luting agent cylinders (height= 1 mm, Ø= 1.2 mm); 2) fatigue behavior, ceramic discs paired and bonded onto fiber-epoxy resin discs (Ø= 10 mm, 2.

The Influence of Extra-Fine Milling Protocol on the Internal Fit of CAD/CAM Composite and Ceramic Crowns.

This study aimed to evaluate the marginal and internal adaptation of CAD/CAM crowns milled using two different milling protocols (fine or extra-fine) within a 4-axis milling machine. The crowns were fabricated from lithium disilicate ceramic (IPS e.max CAD) and resin composite (Tetric CAD), assessing their fit in various regions.

The impact of the filling technique with two sealers in bulk or associated with gutta-percha on the fatigue behavior and failure patterns of endodontically treated teeth.

Background: The present study aimed to evaluate the fatigue behavior of teeth filled with a calcium silicate-based sealer (Bio-C Sealer, BC) or an epoxy resin-based sealer (AH Plus, AH), in bulk or associated with gutta-percha as main core material.

Methods: Seventy-two sound human maxillary anterior teeth were initially selected. Sixty of them, were randomly chosen, and had their root canals prepared using nickel-titanium reciprocating instruments, being again randomly assigned to five experimental groups ( = 12): C+ (control + prepared but not filled); BC-B (BC in bulk); BC-GP (BC+ gutta-percha); AP-B (AH in bulk); AP-GP (AH+ gutta-percha).

Optical properties of advanced lithium disilicate.

Background: A variety of firing protocols are available for the IPS e.max lithium disilicate (LD) and can be used for new, 'advanced' LD (ALD). However, the impact of firing protocols on the optical properties of ALD is still unknown.

Comparative Strength Study of Indirect Permanent Restorations: 3D-Printed, Milled, and Conventional Dental Composites.

: Limited research has been performed to assess the strength of resin-bonded 3D-printed restorations. Based on that, this study investigates the impact of different manufacturing methods on the fracture load of indirect composite restorations (ICRs) following an aging process. : Three manufacturing techniques-conventional (CRC), milled (MRC), and printed (PRC)-were evaluated using 60 specimens, each with a diameter of 10 mm and a thickness of 1.

Mechanical Properties of Additive-Manufactured Composite-Based Resins for Permanent Indirect Restorations: A Scoping Review.

The introduction of 3D printing technology in dentistry has opened new treatment options. The ongoing development of different materials for these printing purposes has recently enabled the production of definitive indirect restorations via 3D printing. To identify relevant data, a systematic search was conducted in three databases, namely PubMed, Scopus, and Web of Science.

Effect of erosive conditions on different sealant materials used in paediatric dentistry.

To evaluate the effect of acidic challenge on erosion depth and topographic characteristics of different materials used as occlusal sealants. Two hundred specimens of five sealant materials (Fuji IX, Ketac Molar, Fuji II, Equia and Clinpro) and forty bovine teeth enamel samples (control) were prepared and exposed to acidic challenge. The specimens were immersed in four different solutions (orange juice, coke drink, citric acid or distilled water) under mildly shaken conditions for 3 days.

How do different intraoral scanners and milling machines affect the fit and fatigue behavior of lithium disilicate and resin composite endocrowns?

The aim of this in vitro study was to evaluate the effect of the combinations of two different intraoral scanners (IOS), two milling machines, and two restorative materials on the marginal/internal fit and fatigue behavior of endocrowns produced by CAD-CAM. Eight groups (n= 10) were considered through the combination of TRIOS 3 (TR) or Primescan (PS) IOS; 4-axes (CR; CEREC MC XL) or 5-axes (PM; PrograMill PM7) milling machines; and lithium disilicate (LD; IPS e.max CAD) or resin composite (RC; Tetric CAD) restorative materials.

Advancements in Dental Care: The Evolving Landscape of Prosthetic Dentistry.

In the dental field, the specialty of prosthodontics stands out as the frontline of innovation, continually pushing the boundaries to enhance both function and aesthetics for optimal oral rehabilitation [...

Influence of CAD-CAM milling strategies on the outcome of indirect restorations: A scoping review.

Statement Of Problem: The influence of computer-aided manufacturing (CAM) parameters and settings on the outcomes of milled indirect restorations is poorly understood.

Purpose: The purpose of this scoping review was to summarize the current CAM systems, parameters, and setting changes, and their effects on different outcomes of milled indirect restorations and aspects related to their manufacture.

Material And Methods: The protocol of this review is available online (https://osf.

Effect of brushing simulation on the wear behavior of repaired CAD-CAM restorations.

Objective: The aim of the present study was to evaluate the influence of multidirectional brushing on the surface roughness, morphology, and bonding interface of resin-repaired CAD-CAM ceramic and composite restorations.

Materials And Methods: Twelve (N = 12) blocks (4 mm × 4 mm × 2 mm for parallel axis; 5 mm × 4 mm × 2 mm for perpendicular axis) of lithium disilicate glass-ceramic (IPS e.max CAD, Ivoclar AG) and CAD-CAM resin composite (Tetric CAD, Ivoclar AG) were obtained and repaired with direct resin composite (Clearfil AP-X, Kuraray).

Repair protocols for indirect monolithic restorations: a literature review.

Despite the advancements in indirect monolithic restorations, technical complications may occur during function. To overcome this issues, intraoral repair using resin composite is a practical and low-cost procedure, being able to increase the restoration's longevity. This review aimed to evaluate the need for repair and suggest a standardized repair protocol to the main indirect restorative materials.

Repair of monolithic zirconia restorations with different direct resin composites: effect on the fatigue bonding and mechanical performance.

Objective: The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites.

Materials And Methods: Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable).

Impact of try-in paste removal on the fatigue behavior of bonded lithium disilicate ceramics.

This in vitro study assessed the effectiveness of three cleaning protocols (air-water spray, 37% phosphoric acid, or Ivoclean) on lithium disilicate restorations' fatigue behavior after try-in paste application, compared to a clean condition. Lithium disilicate discs (IPS e.max CAD, Ivoclar) with Ø-= 12 mm and 1 mm thickness were prepared from prefabricated CAD-CAM blocks, polished, subjected to CAD-CAM milling topography simulation and crystallization.

Cyclic fatigue of a repaired 4 YSZ ceramic: Effect of the repair protocol on the adhesive and mechanical behavior.

Objective: To evaluate the effect of different surface treatments on the morphology, shear bond, and flexural fatigue strength of a repaired translucent zirconia.

Methods: Monolithic disc-shaped specimens of translucent zirconia were prepared and ground to simulate repair areas. Four groups underwent different treatments: Air-MDP (air-abrasion with alumina particles and 10-MDP primer), -Sil (silica-coated alumina particles with MDP-containing silane), -MDP (silica coating with 10-MDP primer), and Uni adhe (universal adhesive).

Conventional-, bulk-fill- or flowable-resin composites as prosthetic core build-up: Influence on the load-bearing capacity under fatigue of bonded leucite-reinforced glass-ceramic.

This study aimed to evaluate the fatigue performance of simplified ceramic restorations (leucite-reinforced glass ceramic) adhesively cemented onto substrates of different resin composites. Three options from the same commercial line were selected (Tetric N-Line, Ivoclar), classified as Conventional (CRC), Bulk-fill (BRC) and Flowable (FRC), which were used to make discs using a cylindrical metallic device (n = 19; Ø = 10 mm, thickness = 2.0 mm).

Effect of abutment screw-access hole on the fatigue performance of implant-supported lithium-disilicate luted simplified restorations.

The present study aimed to evaluate the impact of the existence of an abutment screw-access hole and the filling effects on the fatigue mechanical behavior of a luted lithium-disilicate glass-ceramic. Seventy-two discs (Ø = 10 mm, 1.0 mm in thickness) of lithium disilicate (IPS e.

Influence of coloring techniques on the surface characteristics and color stability of a monolithic zirconia ceramic.

Statement Of Problem: The color of monolithic zirconia restorations is obtained by presintering or postsintering coloring techniques. However, studies on the differences in surface characteristics and their influence on color stability are lacking.

Purpose: The purpose of this in vitro study was to evaluate the influence of shading and staining techniques for a zirconia ceramic on the surface characteristics and colorimetric parameters (color difference, translucency, and whiteness index) after exposure to coffee or red wine and then polishing.

Ceramic surface conditioning, resin cement viscosity, and aging relationships affect the load-bearing capacity under fatigue of bonded glass-ceramics.

This study aimed to evaluate the influence of ceramic surface treatments, resin cement viscosities, and storage regimens on the fatigue performance of bonded glass-ceramics (lithium disilicate, LD; feldspathic, FEL). Ceramic discs (Ø = 10 mm; thickness = 1.5 mm) were allocated into eight groups per ceramic (n = 15), considering three factors: "ceramic surface treatment" in two levels - 5% hydrofluoric acid etching and silane-based coupling agent application (HF), or self-etching ceramic primer (E&P); "resin cement viscosity" in two levels - in high or low viscosity; and "storage regimen" in two levels - baseline, 24 h to 5 days; or aging, 180 days + 25,000 thermal cycles.

Weak adhesion between ceramic and resin cement impairs the load-bearing capacity under fatigue of lithium disilicate glass-ceramic crowns.

Objective: To evaluate the fatigue behavior of lithium disilicate crowns with a simplified anatomy against progressive cement/ceramic debonding scenarios.

Materials And Methods: Lithium disilicate crowns were fabricated via CAD/CAM and luted onto a dentin analogue material using resin cement following the manufacturer's instructions. Then, the different crown regions were isolated with paraffin oil for the absence of chemical adhesion according to four experimental groups (n = 15): Shoulder; Shoulder + Axial; Fully isolated; and Control (no insulation/fully bonded).

Effect of the region of the CAD/CAM block on the flexural strength and structural reliability of restorative materials.

The aim of the study was to evaluate whether the region (internal or external) of the CAD/CAM block influences the mechanical performance of restorative materials. Blocks of different CAD/CAM materials (Composites: KAV - Katana Avencia; LULT - LULT Ultimate; Ceramics: ENAM - Vita Enamic; NICE - N!CE; EMP - IPS Empress CAD; VMII - Vita Mark II; EMAX - IPS e.max CAD) were selected, and direct resin composite blocks (APX - Clearfil AP-X; FSUP - Filtek Supreme) were built using the incremental technique on a mold from one of the CAD/CAM blocks.

Pigmentation techniques of a 4YSZ: Effect on the fatigue mechanical behavior of a 4YSZ adhesively luted onto dentin analog.

Objective: To characterize the effect of pigmentation techniques on the fatigue behavior of a 4YSZ ceramic adhesively luted onto dentin analog (glass fiber-reinforced epoxy resin).

Methods: 4YSZ ceramic discs (Ø= 10 mm, 1 mm thickness) were allocated into 5 groups: Ctrl - unshaded (IPS e.max ZirCAD MT BL); Manuf - shaded by the manufacturer (IPS e.

Cyclic fatigue vs static loading for shear bond strength test of lithium disilicate and dentin substrates: A comparison of resin cement viscosities.

Objective: To explore the effect of resin cement viscosities on the shear bond strength under static and fatigue load of lithium disilicate and dentin substrates.

Methods: Bonded tri-layer samples (lithium disilicate ceramic cylinder, resin cement, and substrate - ceramic or dentin) was performed considering 2 factors (n = 15): "resin cement viscosity" (high, HV; or low, LV) and "loading mode" (static, s-SBS; or fatigue shear bond strength, f-SBS). The specimens were subjected to s-SBS (1 mm/min, 1 kN load cell) and f-SBS (cyclic fatigue, initial load: 10 N; step-size: 5 N; 10,000 cycles/step; underwater).

Mechanical characterization of a multi-layered zirconia: Flexural strength, hardness, and fracture toughness of the different layers.

This study compared the flexural strength under monotonic (static - sσ) and cyclic load application (fatigue - fσ), hardness (H) and fracture toughness (K) of different layers of a multi-layered zirconia (IPS e.max ZirCAD MT Multi, Ivoclar). Each layer was sectioned, classified into three groups according to yttria content (4-YSZ, 4/5-YSZ and 5-YSZ), and shaped on samples for flexural strength and fracture toughness tests (bars: 1.