Ultrafast Spectroscopy and Red Emission from β-Ga2O 3/β-Ga 2S 3 Nanowires.

Ultrafast pump-probe and transient photoluminescence spectroscopy were used to investigate carrier dynamics in β-Ga2O3 nanowires converted to β-Ga2O3/Ga2S3 under H2S between 400 to 600 °C. The β-Ga2O3 nanowires exhibited broad blue emission with a lifetime of 2.4 ns which was strongly suppressed after processing at 500-600 °C giving rise to red emission centered at 680 nm with a lifetime of 19 μs.

Optical characterization of varnish films by spectroscopic ellipsometry for application in artwork conservation.

The specific aim of this paper is to measure the optical constants of fresh varnish layers up to a thickness of 10 mum by spectroscopic ellipsometry. It is the first time that this technique has been used in artwork conservation and it may prove very promising due to its nondestructive character. Samples of fresh dammar varnish (natural resin) and Paraloid B72 (synthetic resin) applied on glass and carbon black acrylic paint were analyzed.