Characterization of Optimized Ternary PLA/PHB/Organoclay Composites Processed through Fused Filament Fabrication and Injection Molding.

The aim of this study was to investigate the structure-properties relationship of ternary blends of polylactide/polyhydroxybutyrate (PLA/PHB)/organo-modified layered silicate (OMLS). Morphological, thermal, rheological, and mechanical characterizations were performed to understand the influence of OMLS on PLA/PHB (70/30 wt%) formulations optimized through modifications with an epoxy-based chain extender, the use of a plasticizer, as well as the influence of the type of processing route: injection molding or fused filament fabrication. The addition of OMLS allowed the blend compatibility to be improved, with the appearance of a single melting peak on DSC thermograms at 146 °C, as well as the reduction in the size of the nodules for the injected molded specimens.

Chemical Recycling of Vacuum-Infused Thermoplastic Acrylate-Based Composites Reinforced by Basalt Fabrics.

The objective of this work was to compare the material recovered from different chemical recycling methodologies for thermoplastic acrylate-based composites reinforced by basalt fabrics and manufactured by vacuum infusion. Recycling was done via chemical dissolution with a preselected adapted solvent. The main goal of the study was to recover undamaged basalt fabrics in order to reuse them as reinforcements for "second-generation" composites.

Development of Bionanocomposites Based on Poly(3-Hydroxybutyrate-co-3-Hydroxyvalerate)/PolylActide Blends Reinforced with Cloisite 30B.

In the present study, poly(3-hydroxybuturate-co-3-hydroxyvalerate) (PHBV) and plasticized polylactide acid (PLA) blends were processed by melt extrusion with different weight ratio (up to 20 wt.% of PHBV). Bionanocomposites were obtained through the incorporation of an organomodified montmorillonite (C30B) at 3 wt.

New Biosourced Flame Retardant Agents Based on Gallic and Ellagic Acids for Epoxy Resins.

The aim of this work was an investigation of the ability of gallic (GA) and ellagic (EA) acids, which are phenolic compounds encountered in various plants, to act as flame retardants (FRs) for epoxy resins. In order to improve their fireproofing properties, GA and EA were treated with boric acid (to obtain gallic acid derivatives (GAD) and ellagic acid derivatives (EAD)) to introduce borate ester moieties. Thermogravimetric analysis (TGA) highlighted the good charring ability of GA and EA, which was enhanced by boration.

Tannin Gels and Their Carbon Derivatives: A Review.

Tannins are one of the most natural, non-toxic, and highly reactive aromatic biomolecules classified as polyphenols. The reactive phenolic compounds present in their chemical structure can be an alternative precursor for the preparation of several polymeric materials for applications in distinct industries: adhesives and coatings, leather tanning, wood protection, wine manufacture, animal feed industries, and recently also in the production of new porous materials (i.e.

Sodium alginate adhesives as binders in wood fibers/textile waste fibers biocomposites for building insulation.

Alginate derived from seaweed is a natural polysaccharide able to form stable gel through carbohydrate functional groups largely used in the food and pharmaceutical industry. This article deals with the use of sodium alginate as an adhesive binder for wood fibres/textile waste fibres biocomposites. Several aldehyde-based crosslinking agents (glyoxal, glutaraldehyde) were compared for various wood/textile waste ratios (100/0, 50/50, 60/40, 70/30 and 0/100 in weight).